Effects of Mg3(PO4)2 Addition on the Crystal Structure, Mechanical and Thermophysical Properties of CaZr4P6O24 Ceramics
Yang Wang,Yuanyuan Zhou,Chunlan Su,Na Tong,Zhuoqun Han,Futian Liu
DOI: https://doi.org/10.1016/j.jallcom.2019.07.260
IF: 6.2
2019-01-01
Journal of Alloys and Compounds
Abstract:A novel series of CaZr4(PO4)(6)-x wt.% Mg-3(PO4)(2) (x = 0, 2, 4, 6, 8, and 10) ceramics was prepared via a co-precipitation method. The crystal structure, sintering characteristics, and mechanical and thermophysical properties of the Mg-3(PO4)(2) modified CaZr4(PO4)(6) ceramics were investigated. All the samples possessed a pure CaZr4(PO4) 6-type rhombohedral structure. The crystal structure analysed by Rietveld refinement revealed that the lattice parameter a increased, whereas c and the unit cell volume decreased with increasing Mg-3(PO4)(2). Meanwhile, the addition of Mg-3(PO4)(2) distorted the PO4 tetrahedron and ZrO6 octahedron. The sinterability was improved by increasing the Mg-3(PO4)(2) content, and the flexural strength and Vickers hardness monotonically increased to 74.5 MPa and 2.71 GPa, respectively. The thermal expansion varied from -2.27 to -0.37 x 10(-6)/degrees C with increasing Mg-3(PO4)(2) content. All compositions showed a low thermal conductivity, in the range of 0.44-0.56 W m(-1) degrees C-1 from room temperature to 1000 degrees C. Near-zero thermal expansion combined with extraordinary mechanical properties provide ideal materials for low-thermal-expansion applications. (C) 2019 Elsevier B.V. All rights reserved.