Sodium control in Ultrathin Cu(In,Ga)Se2 solar cells on transparent back contact for efficiencies beyond 12%

Yong Li,Guanchao Yin,Yao Gao,Tristan Köhler,Jan Lucaßen,Martina Schmid

DOI: https://doi.org/10.1016/j.solmat.2021.110969

IF: 6.9

2021-05-01

Solar Energy Materials and Solar Cells

Abstract:<p>Ultrathin Cu(In,Ga)Se₂ (CIGSe) solar cells on transparent conductive oxide (TCO) back contacts combine advantages of ultrathin cells for reducing material consumption of rare indium and gallium and TCO-transparency benefited applications in tandems, bifacial configurations etc. However, their efficiencies are still limited and the back barrier potential is a primary reason from an electrical perspective. In this work, we explore the effects of Nadoping by post deposition treatment (PDT) on the performance of ultrathin CIGSe solar cells on ITO (Sn:In₂O₃)-coated Na-free glass substrates. Na doping enhances not only the open circuit-voltage (<em>V</em>_<em>oc</em>) by increasing the doping level, but also the fill factor (<em>FF</em>) by switching the Schottky contact to an Ohmic contact at the CIGSe/ITO interface, which we propose is due to the increased recombination at the back interface. The optimum performance is achieved at a NaF dose of 2 mg with a top efficiency of 12.9%, which exhibits an enhancement by nearly 48% relative compared to the references without Na doping. To our best knowledge, this is the highest efficiency achieved for ultrathin cells (&lt;500 nm absorber thickness) on TCO without additional antireflection or back reflecting layer. Therefore, the results show that sodium control offers a solid basis for the development of ultrathin CIGSe cells on TCO in above-mentioned promising applications.</p>

materials science, multidisciplinary,physics, applied,energy & fuels

What problem does this paper attempt to address?

This paper aims to solve the efficiency problem of ultrathin Cu(In,Ga)Se₂ (CIGSe) solar cells on the transparent conductive oxide (TCO) back contact. Specifically, although these ultrathin CIGSe solar cells have the advantages of reducing the consumption of the rare materials indium and gallium and providing transparency in applications such as tandem and bifacial configurations, their efficiency is still limited, mainly due to the poor electrical performance caused by the back - barrier potential. In order to improve the efficiency of these cells, the researchers explored the effect of introducing sodium (Na) doping through post - deposition treatment (PDT) on the performance of ultrathin CIGSe solar cells. It was found that an appropriate amount of Na doping can not only increase the open - circuit voltage (Voc) by increasing the doping level, but also improve the fill factor (FF) by converting the Schottky contact at the CIGSe/ITO interface into an ohmic contact. Finally, when the NaF dose was 2 mg, the highest efficiency of the cell reached 12.9%, which was a relative increase of nearly 48% compared with the Na - undoped reference cell. This is the highest efficiency achieved so far for TCO - based ultrathin cells (absorber layer thickness < 500 nm) without additional anti - reflection or back - reflection layers. Therefore, this study shows that controlling sodium can lay a solid foundation for the development of ultrathin CIGSe cells in the above - mentioned applications.