Abstract:In preparing Cu2ZnSnSe4 (CZTSe) thin films, selenization at high Se pressure is likely to form a thick molybdenum diselenide (MoSe2) layer. An excessively thick MoSe2 layer degrades the performance of CZTSe solar cells. Annealing under low Se pressure has been suggested to prevent the formation of such a thick MoSe2 layer. However, the potential loss of Sn metal from CZTSe thin films at low Se pressure or high temperature raises the additional difficulty of controlling the compositions and phases of the films. Carefully controlling these selenization parameters to yield high-quality CZTSe thin films is important. This study investigates the loss of Sn and the formation of molybdenum diselenide in CZTSe thin films at low Se pressure. Three-step selenization at low Se pressure is performed on an electrodeposited Cu/Sn/Zn precursor to prepare high-quality CZTSe thin films. In the first step, rapid thermal annealing with a substrate temperature of 500°C and a low Se vapor pressure of 4.6Pa was performed to reduce the loss of Sn and the thickness of the MoSe2 layer, and thus to obtain a Cu-poor and Zn-rich film. In the second step, a high annealing temperature of 570°C and an inert gas at high pressure was used to improve elemental diffusion and increase the uniformity of the elemental distribution. In the third step, thermal annealing with a substrate temperature of 500°C and a low Se vapor pressure of 4.6Pa was performed to reduce the loss of Sn and the thickness of the MoSe2 layer, and to eliminate the impurity phase of SnSe (which was formed in the second step of annealing) on the surface of the CZTS films. The loss of Sn and the formation of molybdenum diselenide in the CZTSe thin films are negligible when this three-step selenization at low Se pressure is used. When the selenization parameters are properly controlled, CZTSe solar cells with an efficiency of as high as 8.2% can be obtained.

8.0% Efficient Submicron CuIn(S,Se) 2 Solar Cells on Sn:In 2 O 3 Back Contact via a Facile Solution Process

8.0% Efficient Submicron CuIn(S,Se)2 Solar Cells on Sn:In2O3 Back Contact Via a Facile Solution Process

Solution‐Processed Bifacial Cu(In, Ga)(S, Se)2 Thin Film Solar Cells with a Frontside Power Efficiency of 9.73%

An Efficient S and Se Co-Annealing Strategy for Performance Enhancement of Solution-Processed Submicron CuIn(S,Se)2 Solar Cells

Over 12% Efficient Low-Bandgap CuIn(S, Se)(2) Solar Cells with the Absorber Processed from Aqueous Metal Complexes Solution in Air

Back Contact Plasma Treatment Enables 14.5% Efficient Solution‐Processed CuIn(S,Se)2 Solar Cells

Cuin(S,Se)(2) Thin Films Prepared from A Novel Thioacetic Acid-Based Solution and Their Photovoltaic Application

Rear Interface Engineering in Solution‐Processed Submicron Cu(In,Ga)(S,Se)2 Solar Cells on Transparent Sn:In2O3 Back Contact

Cu Gradient Design to Attain High Efficient Solution-Processed CuIn(S,Se)2 Solar Cells

A Novel Metal Precursor Structure for Electrodepositing Ultrathin CIGSe Thin Film Solar Cell with High Efficiency.

A Facile Molecular Precursor-Based Cu(In,Ga)(S,Se)2solar Cell with 8.6% Efficiency

Over 10% Efficient CuIn(S,Se)2 Solar Cells Fabricated from Environmentally Benign Solution in Air

Sodium Incorporation for Performance Improvement of Solution‐Processed Submicron CuIn(S,Se)2 Thin Film Solar Cells

Preparation of Cu(In,Ga)Se 2 Thin Film Solar Cells by Selenization of Metallic Precursors in an Ar Atmosphere

Fabrication of Cu2ZnSn(S,Se)4 thin film solar cells by selenization of reactively sputtered precursors

Sb2Se3 thin film solar cells in substrate configuration and the back contact selenization

Nanoparticle-induced grain growth of carbon-free solution-processed CuIn(S,Se)2 solar cell with 6% efficiency.

A CZTSe Solar Cell with 8.2% Power Conversion Efficiency Fabricated Using Electrodeposited Cu/Sn/Zn Precursor and a Three-Step Selenization Process at Low Se Pressure

Stable and Efficient CdS/Sb2Se3 Solar Cells Prepared by Scalable Close Space Sublimation

Beyond 10% efficient Cu2ZnSn(S,Se)4 solar cells: Effects of the introduction of SnS powder during selenization process

Reactive Close-Spaced Sublimation Processed CuSbSe2 Thin Films and Their Photovoltaic Application