Preparation and characterization of triangular hollow porous polyacrylonitrile fiber made by coaxial wet spinning

Huiyun Wang,Ping Wang,Yan Zhang,Dongmei Hu

DOI: https://doi.org/10.1002/app.50816

IF: 3

2021-04-09

Journal of Applied Polymer Science

Abstract:<p>Hollow porous fiber with both hollow and mesoporous structural characteristics can play an important role in storage, adsorption, and other fields. Triangular hollow porous fiber was prepared by coaxial wet spinning in this paper. Polyacrylonitrile (PAN) and N‐N dimethylformamide (DMF) were blended to get cortical solution. Polyvinylpyrrolidone (PVP) and DMF were blended to get core solution. Subsequently, coaxial triangular spinneret was adopted to inject solution into coagulation bath for double diffusion and obtain primary fiber. Then PAN‐based triangular fiber with high porosity was prepared after washing and drying. Scanning electron microscopy, nitrogen physical adsorption instrument, thermogravimetric analyzer, and other instruments were used to test and characterize. The results show that the cross‐section of the fiber is triangular and has a sense of luster. The hollow degree of the fiber is as high as 84.17%, and the sheath has three‐level structure with multi‐scale pore diameters, including micropores (200 μm), submicron pores (200 nm), and nanopores (20 nm). Through the range analysis of orthogonal experiment, it is found that the concentration of cortical solution is the main factor affecting the fiber tensile strength. When the concentration of cortical solution is 17%, the concentration of core solution is 10%, the flow rate ratio of cortical solution to core solution is 10:1, and the concentration of coagulation bath is 10%, the fiber tensile strength reaches 1.43 N/mm². The thermal insulation performance of fiber is better than that of silk, cotton and polyester. The results in this paper will provide an experimental foundation for the design and application of hollow porous profiled fibers.</p>

polymer science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to develop a triangular hollow porous polyacrylonitrile (PAN) fiber with high porosity and excellent thermal insulation properties. Specifically, the authors prepared this kind of fiber through co - axial wet - spinning technology and carried out detailed characterization and optimization on its structure and properties. The following are the main problems and goals of the paper:

1. **Developing a new fiber structure**:
- Most of the traditional hollow porous fibers have a circular cross - section, which limits the development of their properties.
- Inspired by special structures in nature (such as the triangular cross - section of silver ant hairs), the authors aim to prepare bionic fibers with high light reflectivity and thermal insulation properties.

2. **Improving the physical and mechanical properties of fibers**:
- Research the influence of different parameters (such as the concentration of the cortex solution, the concentration of the core solution, the solution flow rate ratio, and the concentration of the coagulation bath) on the tensile strength and elongation at break of the fiber.
- Optimize these parameters to obtain the best mechanical properties. For example, under the optimal conditions, the tensile strength of the fiber reaches 1.43 N/mm².

3. **Improving the thermal insulation properties of fibers**:
- Compare the thermal insulation properties of the prepared triangular hollow porous PAN fiber with those of traditional fibers (such as polyester, cotton, silk).
- The results show that the thermal insulation properties of the triangular hollow porous PAN fiber are better than those of other common fiber materials.

4. **Exploring the application potential of fibers**:
- This new type of fiber not only has excellent thermal insulation properties but also has a high light reflectivity, and may have potential applications in the optical field or passive cooling textile materials.

Through the above research, the authors hope to provide experimental basis and technical support for the design and application of hollow porous special - shaped fibers.

### Key formulas

- **Hollowness**:
\[
H_f=\frac{S_h}{S_c}\times100\%
\]
where \( S_h \) and \( S_c \) represent the area of the hollow part of the fiber and the cross - sectional area respectively.

- **Contour degree**:
\[
P = \frac{R - r}{R}\times100\%
\]
where \( R \) and \( r \) represent the diameter of the maximum outer contact circle and the diameter of the minimum inner contact circle of the fiber respectively.

- **Fiber porosity**:
\[
P_f=\left(1-\frac{\rho_f}{\rho_p}\right)\times100\%
\]
where \( \rho_f \) and \( \rho_p \) represent the fiber density and the polyacrylonitrile density respectively.

- **Fiber wall porosity**:
\[
P_w = P_f - H_f
\]

These formulas are used to quantitatively describe the structural characteristics of fibers and provide a basis for subsequent performance analysis.