Abstract:A range of Fe-Cr-Ni alloys are used in nuclear power plants due to their high mechanical strength and corrosion resistance. As a major component of these alloys, Ni contributes to the formation of austenite microstructures. In many nuclear reactor applications the alloys are exposed to ionizing radiation (g-rays) that can continuously decompose water to a range of highly redox active species (such as •OH, H2O2, O2). The change in water chemistry induced by radiation can affect both the general and localized corrosion behaviour of these alloys. In particular, its influence on the susceptibility of an alloy to localized corrosion such as crevice and stress corrosion cracking (SCC) are important for assessment of reactor component aging. As well, corrosion products that dissolve into the reactor coolant can be transported to the reactor core where they can be neutron activated. This can create a radiological hazard for reactor maintenance personnel. Thus, quantifying the rate of general corrosion and the corrosion product transport in a reactor are important safety, operation and maintenance issues. It has been well established that the type of oxide that forms on a surface is a critical factor in determining both general and localized corrosion behaviour. Both alloy composition and water chemistry affect the type of oxide that forms. Systematic studies that examine the effect of alloy composition on corrosion are rare and those available have been conducted mostly from a metallurgical perspective. There are even fewer studies that examine the combined effects of alloy composition and corrosion environment. A fundamental understanding of the mechanism by which the Fe to Ni ratio in a steel alloy influences the corrosion rate in different environments will provide valuable information that can be used for alloy selection and usage. We have investigated the effect of the Fe to Ni ratio of alloy on oxide formation and growth kinetics. For this study, customized steel alloys with different Ni contents and constant Cr content (18 ± 1 %) were prepared. The Ni content ranged from 15 to 25 wt.%, within the range between AISI 316L and Alloy 800 (Fig. 1). The corrosion kinetics was investigated using a combination of coupon corrosion tests and electrochemical measurements. These measurements were augmented by oxide surface and depth analyses using several spectroscopic and imaging techniques, and by post-test solution analyses for dissolved metal loss. We found that the oxide formed at pH 10.6 and 80 °C has a graded layer structure, consisting of a mixed spinel oxide (FeCr2O4/Fe3O4/NiFe2O4) as an inner layer and Ni(OH)2 as an outer layer. The increase in Ni content from 15 to 25 wt.% does not affect the inner layer but increases the thickness of the Ni(OH)2 layer. The increase in Ni content also decreases the total amount of dissolved metal loss. Gamma-irradiation of the corroding system increases the corrosion potential on these alloys. Correspondingly, gamma-radiation accelerates the formation of passive oxide layers and decreases the overall rate of metal dissolution. The observed kinetics of oxide growth and metal dissolution can be explained by the competition kinetics of oxide growth and dissolution for oxidized metals. Figure 1

Impact of some inorganic anions on the corrosion of nickel in a solution containing Na2SO4 and NaClO4

Effect of Sulfate Ions on Anodic Polarization Behavior of Nanocrystalline Copper Bulk

Kinetic Analysis on Anodic Polarization Behavior of Nanocrystalline Copper in Na2SO4 Solution

Effects Of Nitrogen On The Passivation Of Nickel-Free High Nitrogen And Manganese Stainless Steels In Acidic Chloride Solutions

Impact of NaCl impurity on corrosion of 316 L steel in molten nitrate salts for thermal energy storage: An electrochemical study

Electrochemical Study on the Impact of Nacl Impurity on Corrosion of Stainless Steel 316l in Molten Nitrate Salts for Thermal Energy Storage

Corrosion inhibition of aluminum in sodium hydroxide solutions using some inorganic anions

Environmental Factors Affecting the Pitting Corrosion Potential of a Zinc–Titanium Alloy in Sodium Hydroxide Solutions

Electrochemical dissolution of nickel-42 in acid electrolytes

Corrosion of Nickel in Acid Solutions with Hydrogen Sulphide

Corrosion Behavior of Stainless Steels and Nickel-Based Alloys in Acetic Acid Solutions Containing Bromide Ions

Probing the Nickel Corrosion Phenomena in Alkaline Electrolyte Using Tender X-Ray Ambient Pressure X-Ray Photoelectron Spectroscopy

Microstructure and Corrosion Behavior of Electrodeposited Nickel Prepared from a Sulphamate Bath

Effect of Ni on the Ion-Selectivity of Rust Layer on Low Alloy Steel

Effects of Acidity and Alkalinity on Corrosion Behaviour of Al–Zn–Mg Based Anode Alloy

The corrosion behavior of electroless Ni–P coatings in concentrated KOH electrolyte

Stress And Corrosion Performance Of Amorphous Ni-Mo-P Electroless Deposits

Effect of Nickel Content on the Corrosion Behaviour of Stainless Steel at 80 °C

Corrosion Behavior of 9 % Ni Steel for LNG Storage Tanks in 3.5 Wt. % NaCl Solution

Concerning the stability of seawater electrolysis: a corrosion mechanism study of halide on Ni-based anode

Passivation of Ni-Cr and Ni-Cr-Mo Alloys in Low and High pH Sulfate Solutions