Abstract:Tungsten (W) is one of the most promising plasma-facing materials for future fusion devices. Although its melting point is the highest among all metals, it still has great risk of melting under extremely high plasma heat fluxes, which is a big concern for ITER and future reactors. Actively cooled W plasma-facing components (PFCs) with both monoblocks and flat-type structure have been successfully installed in the lower divertor of the EAST tokamak since 2021, and provide a good opportunity for direct comparison of the damage mechanism for the two types of PFCs. Various in situ melting phenomena on the lower divertor have been observed by CCD cameras, which have been further verified by post-mortem inspections. Severe melting and even exfoliation of the edge-beveled W plates were observed on some W/Cu flat-type components at horizontal outer targets. Many droplets were ejected during long-pulse operations, which induced a significant increase of W impurities and total irradiation in the core plasma, and thus greatly deteriorated the plasma performance and even caused disruptions. Two different shaping structures of flat-type PFCs show different positions of melting and the corresponding mechanisms. Slight melting was found on the sharp leading edges of W/Cu monoblocks between cassette modules (inter-CM) for horizontal targets with small droplet ejection, which was much improved compared to that observed on the upper W divertor, illustrating that the application of a large-sized bevel chamfer inter-CM was generally effective. In addition, an unexpected melting phenomenon on the dome plate was attributed to the extreme transient heat flux during disruption with runaway electrons. The application of both types of W/Cu PFCs for the divertor provides important experiences and lessons for the engineering design and optimization of divertor PFCs in future fusion devices.

Interface cracking damage of W/Cu monoblocks as divertor target after high-cyclic plasma discharges in EAST

Progress of High Heat Flux Component Manufacture and Heat Load Experiments in China

Thermal fatigue failure behavior on Be/Cu joint of ITER first wall after enhanced heat flux test

Failure analysis of Be/Cu joint in ITER first wall mock-ups

Failure analysis of damaged tungsten monoblock components of upper divertor outer target in EAST fusion device

Tungsten Joining with Copper Alloy and Its High Heat Load Performance

Characterization of the Crack and Recrystallization of W/Cu Monoblocks of the Upper Divertor in EAST

Nondestructive Testing of East W/Cu Divertor Components

Experiences and lessons from the mitigation of leading edge induced melting on actively cooled ITER-like W/Cu monoblocks for divertor target in EAST

Fatigue and Fracture Analysis on EAST Divertor Monoblock Heat Sink in H-mode Operation

High heat flux test and post examination of ITER divertor W/Cu monoblock mock-ups

In Situ Melting Phenomena on W Plasma-Facing Components for Lower Divertor During Long-Pulse Plasma Operations in EAST

Microstructural analysis of the thermal fatigue tested Be/CuCrZr joint with artificial defects between Ti/Cu interlayers

Experimental and Numerical Simulations of ELM-like Transient Damage Behaviors to Different Grade Tungsten and Tungsten Alloys

Manufacturing and Testing of W/Cu Mono-Block Small Scale Mock-Up for EAST by HIP and HRP Technologies

Overview of Decade-Long Development of Plasma-Facing Components at ASIPP

Power Balance Investigation in Long-Pulse High-Performance Discharges with ITER-like Tungsten Divertor on EAST

Melting of W/Cu flat type component for main limiter and its impact on plasma operation in EAST experiments

Surface Modifications of W Divertor Components for East During Exposure to High Heat Loads with He

Plasma–tungsten Interactions in Experimental Advanced Superconducting Tokamak (EAST)

Overview of R&D on Plasma-Facing Materials and Components in China