Abstract:Experiments are carried out in CIMPLE-PSI, to understand the recrystallization behavior of tungsten (W) exposed under very-high target temperature and ITER relevant long He + -fluence. The effect of helium bubbles on possible retardation of the recrystallization process is also studied. W samples are simultaneously exposed under He plasma and annealed by the plasma heat-load, in contrast to previously reported experiments in literature, which were carried out sequentially. Exposed samples are characterized by field emission scanning electron microscopy (FESEM), Vickers surface micro-hardness, nano-hardness and electron backscattered diffraction (EBSD). It is observed that the sample exposed to plasma under the highest temperature (1866 K) suffered acute retarded grain growth. This also contained small, unrecovered grains on the exposed surface. FESEM imaging of the cross-sections confirm relatively smaller helium bubbles still form even at the very high temperature conditions, which can impede the grain growth locally, whenever they are forming right on the grain boundaries. This results in an inhomogeneous mixture of surface grains with sizes from few micrometer to few tens of micrometer. EBSD estimates that the plasma exposed surface was only 34% recrystallized. The second sample exposed at a lower temperature (1699 K) but for three times higher fluence (ion fluence: 1.19×10 27 m -2 ) was almost fully recrystallized, which shows retardation diminishes very fast with the duration of the exposure. Hardness measurements were undertaken to understand the variation with plasma exposure/annealing temperature and the extent of recrystallization, with three different probing length scales, spanning from few hundreds of nanometer to several micrometers. Both helium plasma exposed W samples are observed to undergo retarded softening up to a depth of few hundred nanometers from the surface, compared to when the metal may be recrystallized by simple heating, without any plasma exposure.

Recovery and recrystallization of warm-rolled tungsten during helium thermal desorption spectroscopy annealing

Retarded Recrystallization of Helium-Exposed Tungsten

A Comparative Study of Surface Modification under Helium Implantation on Mechanically and Electrochemically Polished Tungsten

Role of Helium Bubbles and Voids on the Property of Nanocrystalline Tungsten

Helium Irradiation Effects on the Surface Modification and Recrystallization of Tungsten

Crystal orientation effects on helium ion depth distributions and adatom formation processes in plasma-facing tungsten

Helium effects on the surface and subsurface evolutions in single-crystalline tungsten

Interaction Between Recrystallization and Helium Behavior in Cold-Rolled Nickel

Softening due to Grain Boundary Cavity Formation and its Competition with Hardening in Helium Implanted Nanocrystalline Tungsten

Effect of helium pre-implantation on the thermal shock performance of tungsten

Microstructure Evolution of Pure Tungsten after Low-Energy and High-Fluence He+ Implantation Assessed by Synchrotron Grazing Incidence X-ray Diffraction

Surface Modification of W–V Alloy Exposed to High Heat Flux Helium Neutral Beams

Studies on the retarded recrystallization of tungsten in CIMPLE-PSI exposed under very-high target temperature and long He + -fluence

Microstructure and Helium Irradiation Performance of High Purity Tungsten Processed by Cold Rolling

A Comparative Study on the in Situ Helium Irradiation Behavior of Tungsten: Coarse Grain Vs. Nanocrystalline Grain

Crystallographic Orientation Dependent of Blisters Formation on Tungsten Surface Exposed to Helium Ions

Fuzz Nanostructure and Erosion on Tungsten–vanadium Alloys Exposed to Helium Plasma in the STEP Linear Plasma Device

Morphology and Crystalline Evolution of Tungsten Induced by Low-Energy Helium Ions Irradiation

Mechanisms of helium irradiation blistering and surface deformation in tungsten

Surface Modification and Helium Release of Tungsten Irradiated by 40 Kev Helium Ions

Blistering and Helium Retention of Tungsten and 5% Chromium Doped Tungsten Exposed to 60keV Helium Ions Irradiation