Abstract:Fused silica optics, as key components in high - power laser systems, are prone to be damaged under short - pulse ultraviolet (UV) laser irradiation. CO 2 laser is usually used to repair the laser damage and extend the service life of optics. However, the anti - laser damage characteristics of repaired substrates sometimes can't meet the expectation. To facilitate better application of CO 2 laser repairing method, this work studied the CO 2 laser irradiating mechanism of fused silica in detail and investigated the damage characteristics of repaired optical surface through experiments. Firstly, finite element level - set (FELS) method is adopted to simulate CO 2 laser irradiating process. The simulation showed that CO 2 laser irradiation would cause molten material migration, vapor material deposition and affect the formation of residual stress. Various tests of morphology, residual stress, and photo - thermal absorption were conducted to study the changes of laser damage characteristics of repaired craters. The experimental results presented that molten materials migration and vapor materials re deposition occurred in CO 2 laser irradiation, which would promote the formation of residual stress, cause stronger laser absorption, or even induce laser damage. Through the experiment, accuracy of simulation was verified further. In this work, the CO 2 laser repairing mechanism of fused silica and laser damage characteristics of repaired optics are clarified through FELS simulation and experiments. Relative results can provide a certain technical support for the performance improvement of repaired fused silica optics.

Damage characteristics of fused silica under low-temporal coherence light

Self-focusing and stimulated Brillouin scattering effect of low-temporal coherence light and corresponding damage characteristics in fused silica

Bulk Damage and Stress Behavior of Fused Silica Irradiated by Nanosecond Laser

Correlation Between Photoluminescence Properties of Surface Defects and Laser-Induced Damage Threshold of Fused Silica

Laser Induced Damage in Fused Silica for 248 nm

The Influence of Co2 Laser Local Irradiation on the Laser Damage Resistance of Fused Silica

Scan Speed and Fluence Effects in Femtosecond Laser Induced Micro/nano-Structures on the Surface of Fused Silica

The Structure Evolution of Fused Silica Induced by CO 2 Laser Irradiation

Material migration and damage characteristics of fused silica optical surface treated by CO 2 laser/short – pulse ultraviolet laser

Dynamics of filamentary damage induced by nanosecond laser in fused silica

Damage Behaviors of Silica Microparticles on Fused Silica Optics under 355 Nm High Fluence Laser

Laser-induced defects in fused silica by UV laser irradiation

Theoretical and Experimental Investigations of Localized CO2 Laser-Fused Silica Interactions and Thermo-Mechanical Properties of Mitigated Sites

Near-Infrared Femtosecond Laser Induced Defect Formation in High Purity Silica below the Optical Breakdown Threshold

Surface Damage Mitigation of Fused Silica with CO2 Laser

Damage Induced 0n Fused Silica by Fundamental Frequency and Third Harmonic of Nd:YAG Laser

An Investigation into the Densification-Affected Deformation and Fracture in Fused Silica under Contact Sliding

Development of Damage Growth Mitigation in Fused Silica by CO2 Laser

Research Development of CO2 Laser Treatment for Repair Damage in Fused Silica

Influence of Ambient Temperature on Nanosecond and Picosecond Laser-Induced Bulk Damage of Fused Silica

Combined non-destructive evaluation of the damage precursors in fused silica optics