Abstract:The diameters of asphalt concrete cylindrical specimens typically measure either 100 mm or 150 mm, as these are the standard sizes for almost all conducted tests. However, the impact of specimen size on the fracture performance of asphalt mixtures has not been extensively explored. This study aimed to address this gap by performing laboratory tests on semi-circular bending (SCB) specimens. These tests were designed to apply the Size Effect Law (SEL) in evaluating the fracture performance of two asphalt mixture types (AC10 and AC16) at-10 degree celsius. The experiment selected four different diameters (76 mm, 100 mm, 125 mm, and 150 mm) and two notch-radius ratios (alpha 0 0 = 0.2 and 0.4) to investigate the relationship between the specimen dimensions and both the nominal stress and fracture toughness (KIC). K IC ). Results indicated that the nominal stress and K IC adhered to the SEL. It was observed that both aggregate gradation and notch-radius ratio (alpha 0) 0 ) significantly influenced the SEL's effect on nominal stress. An increase in alpha 0 0 from 0.2 to 0.4 shifted the fracture failure towards a more linear elastic fracture behavior. Specifically, the coarser gradation in AC16, compared to AC10, predisposed the fractures towards linear elastic behavior. Moreover, an increase in alpha 0 0 notably augmented the brittleness number. For specimens with identical dimensions and alpha 0, 0 , AC16 exhibited higher D / D 0 values, indicating a stronger alignment with Linear Elastic Fracture Mechanics (LEFM) principles for the tested specimen sizes compared to AC10. As the size of the specimen increased, there was a gradual rise in K IC , with the enlargement from 76 mm to 150 mm resulting in K IC increases of 25.2 % and 12 % for alpha 0 0 values of 0.2 and 0.4, respectively, in the AC10 mixture. Conversely, the AC16 mixture saw respective enhancements of 15.8 % and 7.6 % for the same alpha 0 0 values. The influence of alpha 0 0 on the apparent fracture toughness became less pronounced with its increase; K IC gradually decreased for AC10, yet increased for AC16 with rising alpha 0 0 levels. For the same asphalt mixture type, K IC was found to escalate with both D / D ' 0 and alpha 0. 0 . At an alpha 0 0 of 0.4, the disparities between K Ic and K Ic m , - expressed as (KIc K Ic m- K Ic )/ K Ic m , - stood at 13.9 % and 9.2 % for AC10 and AC16, respectively, with a diameter of 150 mm. Based on these findings, it is recommended to utilize an SCB specimen with a diameter of 150 mm and an alpha 0 0 of 0.4 for fracture performance testing, as these parameters appear to provide the reliable assessment of the materials' fracture behavior.

Effect of SCB specimen size on mode I fracture parameters of asphalt concrete at low and intermediate temperatures

Fracture Behavior of Asphalt Pavement with Cracked Base Course under Low Temperature

Impact of SCB Specimen Size, Temperature, Loading Rate, and Loading Mode on Fracture Behavior of Asphalt Mixture Using Response Surface Method

Experimental Study on the Anti-Cracking Performance for High Viscoelastic Asphalt Sand with SCB

Effect of specimen size on mode I fracture performance of hot mix asphalt at the low temperature

Evaluation of Test Methods for Fracture Resistance of High Modulus Asphalt Binders from Rheological and Mechanical Perspectives

Low Temperature Performance Evaluation of Asphalt Binders and Mastics Based on Relaxation Characteristics

Size Effect Analysis of Mode I Fracture Performance of Hot Mix Asphalt

Study on mechanical properties of AR-SAMI

Compaction method and specimen geometry effect on the fracture properties of asphalt concrete in the SCB test at intermediate temperature

Assessment of fracture criteria for cracking behavior of asphalt concrete using various SCB specimen sizes

Effects of moisture contents, fracture modes, and temperatures on fracture toughness and crack distribution of asphalt concrete at low-temperature

Using Overlay Test to Evaluate Fracture Properties of Field-Aged Asphalt Concrete

Fracture strength of warm mix asphalt concretes modified with crumb rubber subjected to variable temperatures

Investigations on the Crack Resistance Characteristics of Asphalt Concrete Based on Digital Image Correlation Method

Extended Finite Element Modeling of Hot Mix Asphalt Based on the Semi-Circular Bending Test

Investigation of fracture performance of asphalt mixtures considering size effect law and equivalent crack propagation law

Experimental and numerical study on the effect of friction between crack faces on fracture parameters of hot mix asphalt concrete

Fracture Properties and Potential of Asphalt Mixtures Containing Graphene Oxide at Low and Intermediate Temperatures

Cracking Analysis of Asphalt Mixture Using Semi-circle Bending Method

Cohesive Zone Modeling of I–II Mixed Mode Fracture Behaviors of Hot Mix Asphalt Based on the Semi-Circular Bending Test