Abstract:Low and intermediate temperature cracking are two key factors for fracture and failure of hot mix asphalt (HMA), which impose huge costs on transportation departments and related agencies around the world. These two kinds of cracking may apear in the short- or long-term owing to states such as freezeing-thawing damage (FTD) and the aging mechanism. On the other hand, due to its unique features, nanomaterials are a suitable option for improving the mechanical features of bituminous mixes, which can affect the short-term performance and long-term performance. In this study, low and intermediate temperature fracture specification of Nano-molybdenum disulfide (MDS)-reinforced hot mix asphalt (HMA) under long-term conditions was evaluated. For this goal, two semi-circular bend (SCB) geometries comprising 90 degree and angled cracks, which were called symmetric SCB and classical-reinforced SCB-2, were made. Then, two various conditions, i.e. three freeze–thaw cycles and six days of aging operation were performed on various mixes in order to simulate the long-term performance of the bituminous mixes. Finally, the HMA samples with and without MDS were subjected to the three-point SCB test at the final temperatures of −15 °C and + 15 °C. The findings demonstrated that mixes comprising 0.3 % and 0.6 % MDS had more increased fracture energy (FE), fracture toughness (K IC ), and stiffness under pure tension at low and medium temperatures (short-term and long-term fracture specification). In fact, MDS caused an increase in the fracture indices by increasing the maximum force (P max ) and displacement at the time of fracture. At ± 15 °C and for the geometry comprising the 90 degree and 35 degree cracks, the HMA and Nano MDS-reinforced HMA mixes had more suitable flexibility under 3 FTC compared to 0 FTC; while, the flexibility of the HMA and Nano MDS-reinforced HMA mixes decreased under aging mechanism. In discussing the long-term performance of HMA mixture (with and without modifiers), the findings showed that applying three FTD's cycles to the mixes caused a decrease in K IC , FE, and P max . Also, reducing the stiffness of various mixes under 3 FTC, and increasing the flexibility of the mixes were other findings of this study. In addition, the simultaneous use of both SCB geometries comprising 90 degree and 35 degree cracks was proposed to study the fracture specification of bituminous mixes owing to the more inferior average FE and K IC . Finally, the application of 3FTC on bituminous mixes can more suitable simulate the long-term performance of asphalt pavement (compared to aging mechanism).

Fracture strength of warm mix asphalt concretes modified with crumb rubber subjected to variable temperatures

Characteristics of Mineral Fillers and Their Effects on Mastic Fracture Resistance at Intermediate Temperature 20 ℃

Improved Methodology to Evaluate Fracture Properties of Warm-Mix Asphalt Using Overlay Test

Experimental Study on the Anti-Cracking Performance for High Viscoelastic Asphalt Sand with SCB

Investigation of the effect of Crumb Rubber Additive on the Fracture of characteristics of asphalt mixtures in control and asphalt rubber mixtures

Effect of SCB specimen size on mode I fracture parameters of asphalt concrete at low and intermediate temperatures

Experimental Investigation of the Fracture Properties for Crumb Rubber Modified (CRM) Asphalt Mixtures

Pure mode I fracture specification of molybdenum disulfide nanoparticles (MDS)-reinforced hot mix asphalt (HMA) under long-term conditions

Evaluation of the influence of warm additives modified by Vestenamer polymer on the performance of stone matrix asphalt containing crumb rubber

Rheology of Crumb Rubber-Modified Warm Mix Asphalt (WMA)

Cracking Resistance of Recycled Rubber Asphalt Binder Composed of Warm-Mix Additives

Investigation of the Effect of Crumb Rubber Powder and Warm Additives on Moisture Resistance of SMA Mixtures

Mechanical Properties and Numerical Analyses of Basalt Fiber Crumb Rubber Mortars in Soft Rock Roadways

Impact of SCB Specimen Size, Temperature, Loading Rate, and Loading Mode on Fracture Behavior of Asphalt Mixture Using Response Surface Method

Rheological and environmental characteristics of crumb rubber asphalt binders containing non-foaming warm mix asphalt additives

Rheological Behaviour of WMA-Modified Asphalt Binders with Crumb Rubber

Performance and Aging Characteristics of Hot Mixture Asphalt with Crumb Rubber and Warm Mix Asphalt Additives

Investigation of cracking mechanisms in rubber-modified asphalt through fracture testing of mastic specimens

Effects of moisture contents, fracture modes, and temperatures on fracture toughness and crack distribution of asphalt concrete at low-temperature

Evaluation of the effect of moisture on behavior of warm mix asphalt (WMA) mixtures containing recycled asphalt pavement (RAP)

Selection of Optimal Warm-Mix Additive for Recycled Crumb-Rubber Modified Asphalt Binder Based on Rheological Tests and Viscoelastic Models