Abstract:Recent research using the semicircular bending (SCB) test with 100 mm diameter specimen cored from gyratory compacted samples demonstrated the suitability of this sample size for testing dense graded asphalt mixes with a nominal maximum aggregate size (NMAS) of up to 19 mm. Alongside the gyratory compactor, the Marshall compactor remains part of current specifications in many countries, including ASTM international standards. The Marshall compactor uses a 4-inch (101.6 mm) mould, which is slightly larger than the gyratory compactor's 100 mm mould, and employs a different compaction effort, resulting in different aggregate orientation. This study investigates potential differences in the fracture properties of SCB test specimens compacted using different methods. Sample thicknesses of 30 , 40 , and 50 mm were evaluated in the SCB test at 25°C under a monotonic loading rate of 1 mm/min. A total of 81 specimens were prepared from three asphalt mixes with NMAS of 14 mm and 20 mm, including two dense graded asphalt mixes and one stone mastic asphalt mix. The fracture properties, including fracture energy, fracture toughness, and cracking resistance index (CRI) were evaluated. The study found that the repeatability, evaluated via the coefficient of variation, ranged from 1.1% to 21.7%, with an average value of 8.3%. A directly proportional relation was observed for indexes from the 100 mm and 150 mm samples using the gyratory compactor. The Marshall compactor specimens yielded higher fracture toughness and fracture energy values, while the CRI values were approximately 1.23 times those obtained from the gyratory compactor. This result shows that different compaction methods have direct effect on the fracture properties of SCB test specimens, emphasising the importance of considering compaction methods for the SCB test when determining the threshold value of cracking resistance for asphalt mixes, especially in the balanced mix design for asphalt mixes.

Experimental Study on the Anti-Cracking Performance for High Viscoelastic Asphalt Sand with SCB

Study On The Anti-Cracking Performance Of Fibrous High-Viscoelastic Asphalt Sand

Analysis on Anti-cracking Performance of High Viscoelastic Tar Sand

Research on the Anti-Cracking Performance of High Viscoelastic Tar Sands

Study on mechanical properties of AR-SAMI

Rheological Behavior of High Modulus Asphalt Binder and Its Indication for Fracture Performances

Evaluation of Test Methods for Fracture Resistance of High Modulus Asphalt Binders from Rheological and Mechanical Perspectives

Study of the Viscoelasticity for Fibrous High ViscoelasticAsphalt Sand

Research On The Crack Resistance Of The High-Viscosity Emulsified Asphalt Sand Seal

Study on Relaxation Damage Properties of High Viscosity Asphalt Sand under Uniaxial Compression

Viscoelastic Fracture Analysis of Asphalt Concrete Pavement with Cracks

Nonlinear Viscoelastoplastic Kinetics for High-Temperature Performance of Modified Asphalt Binders

Experimental Study on Pavement Performances of SBP Modified Asphalt

Micromechanics Modeling of Viscoelastic Asphalt-Filler Composite System with and Without Fatigue Cracks

Cracking Analysis of Asphalt Mixture Using Semi-circle Bending Method

Research on High- and Low-Temperature Rheological Properties of High-Viscosity Modified Asphalt Binder

Viscoelastic Analysis of Asphalt Pavement with Reflective Cracks and Subjected to Dynamic Loading

Extended Finite Element Modeling of Hot Mix Asphalt Based on the Semi-Circular Bending Test

Compaction method and specimen geometry effect on the fracture properties of asphalt concrete in the SCB test at intermediate temperature

Low-temperature fracture resistance of plant-mixed heat recycled asphalt mixture based on SCB

Investigations on the Crack Resistance Characteristics of Asphalt Concrete Based on Digital Image Correlation Method