Abstract:Under the combined effects of ultraviolet, temperature and water, the asphalt pavement would deteriorate gradually. Fog seal technology was an effective strategy of energy conservation, environmental protection and cost reduction for preventive maintenance of asphalt pavement. However, the existing conventional fog seal materials based on asphalt emulsion still could not satisfy sufficient durability and were suffered various surface damages, especially the fatigue and thermal cracking problems. This research investigated the feasibility of applying waterborne acrylate and waterborne polyurethane to further improve the cracking resistance for fog seal technology, as a cleaner modification approach. The compatibility of waterborne acrylate and polyurethane in fog seal materials was observed and Gel permeation chromatography test was carried out to release the constituent mitigation during the chemical interaction between asphalt emulsion and waterborne additive. Additionally, fatigue factor test by dynamic shear rheometer was measured and linear amplitude sweep test was also applied to further evaluate the fatigue cracking resistance. The analyses of thermal cracking resistance at low temperatures were conducted through bending beam rheometer test and shear relaxation test. Finally, the relationship between chemical constituent and cracking resistance was conducted to release the effect of waterborne additive on fog seal material through statistical analysis. It presented that asphalt-additives interaction with polymer network formation improved thermal cracking resistance of fog seal materials, with large molecular size from 3.3% to 7.6%. This research revealed that the waterborne cationic acrylate in styrene-butadiene styrene modified emulsified asphalt presented significant application potential for fog seal technology with synergy effect.

Research On The Crack Resistance Of The High-Viscosity Emulsified Asphalt Sand Seal

Analysis on Anti-cracking Performance of High Viscoelastic Tar Sand

Experimental Study on the Anti-Cracking Performance for High Viscoelastic Asphalt Sand with SCB

Analysis of the Fatigue Crack Propagation Process of the Stress-Absorption Layer of Composite Pavement Based on Reliability

Research on the Anti-Cracking Performance of High Viscoelastic Tar Sands

Study On The Anti-Cracking Performance Of Fibrous High-Viscoelastic Asphalt Sand

Cohesive Cracking Simulation of Asphalt Mixture with Reflective Crack Through Xfem

STUDY ON STRESS INTENSITY FACTOR AFFECTED BY FRICTION COEFFICIENT BETWEEN SURFACE LAYER AND SUBBASE

Study on Relaxation Damage Properties of High Viscosity Asphalt Sand under Uniaxial Compression

Viscoelastic Fracture Analysis of Asphalt Concrete Pavement with Cracks

Study on mechanical properties of AR-SAMI

Dynamic analysis of asphalt pavement with reflective cracking on the soft clay ground

Viscoelastic Analysis of Asphalt Pavement with Reflective Cracks and Subjected to Dynamic Loading

Research on the Influence of Material Composition and Construction Process on the Properties of Emulsified Sand Asphalt Fog Seal

Research on the Anti-Reflective Cracking Performance of a Full-Depth Asphalt Pavement

Cracking investigation on fog seal technology with waterborne acrylate and polyurethane as a clean modification approach

Investigation of the High-Temperature and Rheological Properties for Asphalt Sealant Modified by SBS and Rubber Crumb

Design and Experimental Study of Rubber Gravel Asphalt Seal Coat

Analysis on Mechanical Response of Asphalt Pavement Structure Based on 3 D Viscoelastic Finite Element Method

Comprehensive Laboratory Evaluation of Crack Resistance for an Asphalt Rubber Stress-Absorbing Membrane Interlayer (AR-SAMI)