Abstract:Steel wire ropes will creep under long-term loading, resulting in the deterioration of tensile structure performance. From the perspective of materials science, the creep of steel ropes can be understood as the degradation of their equivalent elastic modulus over time, and there are currently no methods or formulas to quantify this degradation. The main purpose of this paper is to propose a general formula for calculating the equivalent modulus degradation of wire ropes, which will facilitate the assessment of performance variations in tensile structures during service. In this study, an experiment on the degradation of the equivalent elastic modulus of steel wire ropes under long-term loading was conducted. In the experiment, measurements were taken using two types of small-diameter steel wire ropes at three stress levels, with data collected over 20,000 h. The results showed that the degradation of the equivalent elastic modulus transitions from rapid to gradual over time and can be divided into three periods. A universal calculation formula was proposed to conveniently express this degradation law, derived from viscoelastic theory with specific parameters obtained through data fitting. To extend the formula's applicability to a wider range of diameters and stress levels, ANSYS was utilized to develop refined models of steel wire ropes and the parameters were determined by the experimental results. After comparison, it was observed that the differences between the calculated values of the formula and the simulated values of the model were relatively small for small diameters, verifying the accuracy of the proposed formula. However, for larger diameters, significant differences were observed in the early phase of the second period. Consequently, an additional experiment was conducted on a wire rope with a diameter of 18 mm to verify the feasibility of the formula for large diameters. The results showed that the measured values closely matched the simulated values from the model. Based on the simulated values, a revised formula was proposed for largediameter ropes. The two proposed calculation formulas can be used to quickly estimate the degradation of the equivalent elastic modulus of steel wire ropes. Numerical results further demonstrated that due to the degradation of the equivalent elastic modulus of wire ropes, the mechanical performance of the structure significantly deteriorates over time, offering a valuable reference for structural health monitoring and tensile structure evaluation.

Quantitative Study on Cross Section Damage of Steel Wire Rope Based on Magnetic Signal Characteristics Under Weak Magnetic Excitation

Research on Quantitative Detection of Wire Rope Damage Based on Weak Magnetic Excitation

Finite Element Simulation and Test of Metal Magnetic Memory Detection of Wire Rope Under Weak Magnetic Field

Finite Element Analysis of Steel Wire Ropes Considering Creep and Analysis of Influencing Factors of Creep

Influence of the Size of Damage to the Steel Wire Rope on the Magnetic Signature

Distinguish Abnormal Tensile and Torsional Stresses of Steel Wire Rope Using Magnetoelastic Effect.

Simulation analysis and experimental investigation of wire rope leakage magnetic field detection

The Degradation of Equivalent Elastic Modulus of Steel Wire Ropes under Long-Term Loading

Fast Quantitative Method to Detect the Cross-Sectional Loss of Wire Rope Defects

Novel Diagnostic of Steel Wire Rope With Passive Magnetic Methods

Magnetic Flux Leakage Sensing and Artificial Neural Network Pattern Recognition-Based Automated Damage Detection and Quantification for Wire Rope Non-Destructive Evaluation

Wire Rope Defects with the Micro-magnetic NDT Technology

Fatigue damage evaluation and verification of steel wire rope based on magnetic flux leakage

Increasing Detection Resolution of Wire Rope Metallic Cross-Sectional Area Damage Based on Magnetic Aggregation Structure

Structure and Character Analysis of a New Type of Steel Wire Rope NDT Detector Apparatus

Residual magnetic field as a source of information about steel wire rope technical condition

A New Signal Processing Method for the Nondestructive Testing of a Steel Wire Rope Using a Small Device

A Review of Non-Destructive Damage Detection Methods for Steel Wire Ropes

Study of Noise Reduction and Identification of Internal Damage Signals in Wire Ropes

Quantitative Method for Detecting Internal and Surface Defects in Wire Rope

Quantitative Detection of Local Flaw under the Lift-Off Effect for Steel Wire Ropes