Fatigue damage evaluation and verification of steel wire rope based on magnetic flux leakage

Zhen Hu,Mengjuan Dong,Fuyin Jia,Enyuan Wang,Hu, Zhen

DOI: https://doi.org/10.1007/s13349-023-00734-0

2023-10-29

Journal of Civil Structural Health Monitoring

Abstract:Wear and wire fracture are the most common damage and failure modes of steel wire ropes (SWRs) under actual working conditions, which can induce the reduction of effective cross-sectional area and bearing capacity, and seriously affect the service lifespan of SWRs. Therefore, there is a risk of serious accidents and huge economic losses if the damage of the SWR in operation is not detected in time. Magnetic flaw signals of the SWRs can demonstrate its irreversible damage, and the damage evolution is manifested in complex and irregular fluctuations of the signals. In this article, the fatigue damage process of mine hoisting SWRs was simulated and damage signals were collected by non-destructive flaw detector. To evaluate fatigue damage of SWRs effectively, first, this study analyzed the spectrum features of damage signals based on the fast Fourier transform (FFT). In addition, it adopted a robust signal processing method, i.e., wavelet leaders-based multifractal (WLMF), to combine multifractal analysis with detection of bending fatigue damage of a SWR for the first time. The numerical analysis results show that as the number of bending fatigue cycles grows, the spectrum evolves into multiple peaks, and the amplitude corresponding to the dominant frequency expands. Moreover, the width of multifractal spectrum increases and the value range on the Y-axis of the singular spectrum expands synchronously with the number of fatigue cycles. For the damage parameters, an increase in Δ h and a decrease in Δ f indicate that the SWRs damage begins to accelerate and spread quickly. The multifractal spectrum parameters and scale function agree well with the geometric structure characteristics of damage signals. The reliability of the damage parameters is verified by counting the distribution and the number of broken wires under different fatigue cycles. Hence, it is a suitable method for fatigue damage detection and can be effectively applied to status monitoring and fault diagnosis of SWRs.

engineering, civil