Abstract:The combined utilization of mineral accelerators and nano-seeding materials is a novel method to promote the early strength of cement-based materials. In this paper, the effects of nano-C-S-H seed (NCS) on the early compressive strength of the Portland cement (PC)- calcium sulfoaluminate cement (CSA) binder were investigated. The results showed that NCS and CSA synergistically contributed to the early strength of PC. In detail, a 326.3% increase in the 10 h compressive strength of PC paste was obtained through the addition of NCS (2 wt%) and CSA (5%) in common. This was higher than the sum of the increases observed with the single additions of CSA (157.9%) or NCS (87.6%), with the same above dosage, in PC. Meanwhile, the early strength enhancement effects of NCS and CSA, when used together in PC, lasted longer than the effects of either used alone. Moreover, the synergetic effect mechanism was analyzed by isothermal calorimeter, QXRD, TGA, MIP, and SEM techniques. The calorimetry, XRD, and TGA results demonstrated that the synergistic mechanism was associated with the synergistic promotion effects of CSA and NCS on the hydrates. The fast hydration of CSA produced large amounts of ettringite and also consumed partial free water to promote the performance of the seeding effect of NCS which, simultaneously, further accelerated the precipitation of C-S-H gel and CH. The high alkie environment was also beneficial for the continuous generation of ettringite. In addition, the results of MIP and SEM measurements showed that the micro-filling effect of NCS significantly optimized the pore structure of a PC-CSA blend-hardened paste. Thus, the synergistic strength enhancement effects of CSA and NCS on PC were attributed to the matching of the promotion of hydration generation and the optimization of pore structures in hardening cement paste. The results of this article provide a new approach to achieving the rapid development of the early strength of cementitious materials, with potential applications in precast concrete and low-temperature construction.

Synthesizing high-quality C-S-H seeds using the impinging stream precipitation method

Effect of Calcium Silicate Hydrate Seeds on Hydration and Mechanical Properties of Cement

Microstructure Refinement of Calcium-Sulfate-aluminate and Portland Cement (CSA-PC) Hybrids with Accelerated CO2 Curing (ACC)

Effects of C-S-H Seed Prepared by Wet Grinding on the Properties of Cement Containing Large Amounts of Silica Fume

Early-age carbonation mitigation of SSC by CxS minerals: Mechanism and Performances

Preparation of C-S-H seeds from waste glass powder and its effect on early performance of cement paste

C-S-H Seeds Accelerate Early Age Hydration of Carbonate-Activated Slag and the Underlying Mechanism

The Acceleration Mechanism of Nano-C-s-h Particles on OPC Hydration

Synergistic Effect and Mechanism of Nano-C-S-H Seed and Calcium Sulfoaluminate Cement on the Early Mechanical Properties of Portland Cement

Synthesis of C-S-H accelerating admixture and its effect on mechanical and hydration properties of engineering cementious composites

Fibrillar calcium silicate hydrate seeds from hydrated tricalcium silicate lower cement demand

Effect of Synthesis Conditions on Particle Size Morphology, Structure, and Acceleration Performance of C-A-S-H Nanoparticles

The effects of nano-C-S-H with different polymer stabilizers on early cement hydration

A method for the reliable and reproducible precipitation of phase pure high Ca/Si ratio (>1.5) synthetic calcium silicate hydrates (C S H)

Preparation of Nano-Sized C-S-H and Its Acceleration Mechanism on Portland Cement Hydration at Different Temperatures

Characteristics of CSH under carbonation and its effects on the hydration and microstructure of cement paste

Ensemble machine learning and Shapley additive explanations for the ability of C-S-H seeds to accelerate cement hydration

High performance C-A-S-H seeds from fly ash-carbide slag for activating lithium slag towards a low carbon binder

Microstructural Investigation of High-Volume Fly Ash Composites Containing Nano-Calcium Silicate Hydrate Crystals

New method of mix design for self-compacting concrete based on aggregate information

Experimental study on strength and abrasion-resistance enhancement admixture