Preparation of Nano-Sized C-S-H and Its Acceleration Mechanism on Portland Cement Hydration at Different Temperatures

Yanfeng Fang,Limin Zhang,Li Li,Mingyu Zhao,Qing Wang,Yong Mei
DOI: https://doi.org/10.3390/ma16093484
IF: 3.4
2023-05-01
Materials
Abstract:Nano-sized C-S-H, a promising early strength agent, can accelerate the hydration rate of Portland cement and increase the early compressive strength of cement-based composites effectively. Nano-sized C-S-H suspensions with different contents of effective constituent and size distributions were prepared by a convenient coprecipitation method and the microstructures were analyzed by Zeta potential, XRD and FT-IR. The exothermic heat, early mechanical properties, hydration degree and hydration products of cement with/without nano-sized C-S-H cured at different temperatures were studied by hydration exothermic, XRD, SEM and TG analysis. Nano-sized C-S-H with semi-crystalline structures was prepared, and the size of the nano-sized C-S-H seeds showed an obvious increase with an increase in theoretical concentration, and slight precipitation in the suspension was observed when the theoretical concentration was 2%. The XRD, TG and SEM analyses showed that nano-sized C-S-H expedites the reaction of C3S in the first 24 h; therefore, the hydration induction period is obviously shortened. The 8 h, 16 h and 24 h compressive strength of mortars containing nano-sized C-S-H increased by 176.0%, 145.6% and 43.9%, respectively, compared with the reference mortar. The enhancement effects of nano-sized C-S-H at 10 °C were lower than that at 20 °C.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to study the acceleration mechanism of the Portland cement hydration process at different temperatures and its enhancement effect on the early - strength by preparing nano - scale C - S - H (calcium - silicate - hydrate) suspensions with different concentrations and particle size distributions. Specifically, the paper focuses on the following aspects: 1. **Preparation and Stability of Nano - scale C - S - H**: Prepare nano - scale C - S - H suspensions with different concentrations by the co - precipitation method and study their stability and particle size distributions. 2. **Effect of Nano - scale C - S - H on the Cement Hydration Process**: Study the influence of nano - scale C - S - H on the heat release amount, hydration degree and hydration products during the cement hydration process by methods such as heat flow analysis, X - ray diffraction (XRD), scanning electron microscopy (SEM) and thermogravimetric analysis (TG). 3. **Enhancement Effect of Nano - scale C - S - H on the Early - strength of Cement - based Materials**: Evaluate the early - strength enhancement effect of nano - scale C - S - H at different temperatures (20 °C and 10 °C) by testing the flexural strength and compressive strength of mortar and concrete at different ages (8 hours, 16 hours, 24 hours and 72 hours). ### Main Findings of the Paper 1. **Stability and Particle Size Distribution of Nano - scale C - S - H**: - The prepared nano - scale C - S - H suspensions show good stability at lower concentrations (1.0% and 1.5%) without obvious sedimentation. - As the theoretical concentration increases, the average particle size of nano - scale C - S - H increases significantly. When the theoretical concentration reaches 2.0%, the particle size distribution becomes significantly wider and slight precipitation occurs. 2. **Acceleration Effect of Nano - scale C - S - H on the Cement Hydration Process**: - The addition of nano - scale C - S - H significantly shortens the hydration induction period of cement and shifts the second exothermic peak to the left, indicating that nano - scale C - S - H effectively accelerates the hydration reaction of C3S (tricalcium silicate). - Within the first 24 hours, the cumulative heat release amount of the cement paste containing nano - scale C - S - H increases significantly, up to 1.446 times that of the reference paste. 3. **Enhancement Effect of Nano - scale C - S - H on the Early - strength**: - Nano - scale C - S - H significantly improves the compressive strength of mortar in the early stage (8 hours, 16 hours, 24 hours), especially the enhancement effect within the first 24 hours is the most obvious. - The compressive strength of mortar containing 2.0% nano - scale C - S - H at 8 hours, 16 hours and 24 hours is increased by 176.0%, 145.6% and 43.9% respectively. - For concrete, the addition of 5% nano - scale C - S - H suspension increases the compressive strength at the 1 - day age by 28.4% - 33.6%, but the compressive strength at the 3 - day and 28 - day ages decreases slightly. ### Conclusion This paper experimentally studies the acceleration mechanism of nano - scale C - S - H on the Portland cement hydration process and its enhancement effect on the early - strength. The results show that nano - scale C - S - H can significantly improve the mechanical properties of cement - based materials in the early stage, especially under low - temperature conditions (such as 10 °C), and its enhancement effect is more obvious. However, an excessively high nano - scale C - S - H concentration will lead to an increase in particle size and a decrease in stability, thus affecting its enhancement effect. Therefore, optimizing the concentration and particle size distribution of nano - scale C - S - H is of great significance for practical applications.