Abstract:The combined utilization of mineral accelerators and nano-seeding materials is a novel method to promote the early strength of cement-based materials. In this paper, the effects of nano-C-S-H seed (NCS) on the early compressive strength of the Portland cement (PC)- calcium sulfoaluminate cement (CSA) binder were investigated. The results showed that NCS and CSA synergistically contributed to the early strength of PC. In detail, a 326.3% increase in the 10 h compressive strength of PC paste was obtained through the addition of NCS (2 wt%) and CSA (5%) in common. This was higher than the sum of the increases observed with the single additions of CSA (157.9%) or NCS (87.6%), with the same above dosage, in PC. Meanwhile, the early strength enhancement effects of NCS and CSA, when used together in PC, lasted longer than the effects of either used alone. Moreover, the synergetic effect mechanism was analyzed by isothermal calorimeter, QXRD, TGA, MIP, and SEM techniques. The calorimetry, XRD, and TGA results demonstrated that the synergistic mechanism was associated with the synergistic promotion effects of CSA and NCS on the hydrates. The fast hydration of CSA produced large amounts of ettringite and also consumed partial free water to promote the performance of the seeding effect of NCS which, simultaneously, further accelerated the precipitation of C-S-H gel and CH. The high alkie environment was also beneficial for the continuous generation of ettringite. In addition, the results of MIP and SEM measurements showed that the micro-filling effect of NCS significantly optimized the pore structure of a PC-CSA blend-hardened paste. Thus, the synergistic strength enhancement effects of CSA and NCS on PC were attributed to the matching of the promotion of hydration generation and the optimization of pore structures in hardening cement paste. The results of this article provide a new approach to achieving the rapid development of the early strength of cementitious materials, with potential applications in precast concrete and low-temperature construction.

Effect of Calcium Silicate Hydrate Seeds on Hydration and Mechanical Properties of Cement

Preparation of C-S-H seeds from waste glass powder and its effect on early performance of cement paste

Fibrillar calcium silicate hydrate seeds from hydrated tricalcium silicate lower cement demand

Effects of C-S-H Seed Prepared by Wet Grinding on the Properties of Cement Containing Large Amounts of Silica Fume

Characteristics of CSH under carbonation and its effects on the hydration and microstructure of cement paste

Effect of C–S–H seeds on the hydration reaction of Portland cement matrices blended with a high-carbon content rice husk ash

Synergistic Effect and Mechanism of Nano-C-S-H Seed and Calcium Sulfoaluminate Cement on the Early Mechanical Properties of Portland Cement

Effect of n-C-S-H on Hydration and Reinforcement of Mineral Powder-Cement System at Low Temperatures

Influence of C–S–H seed and sodium sulfate on the hydration and strength of limestone calcined clay cement

The effects of nano-C-S-H with different polymer stabilizers on early cement hydration

Preparation of Nano-Sized C-S-H and Its Acceleration Mechanism on Portland Cement Hydration at Different Temperatures

Morphological Effect of C–S–H Gel on the Elastic Behaviour of Early-Age Cement-Based Materials

The Acceleration Mechanism of Nano-C-s-h Particles on OPC Hydration

C-S-H Seeds Accelerate Early Age Hydration of Carbonate-Activated Slag and the Underlying Mechanism

Effects of nano-C-S-H seed crystal on early-age hydration process of Portland cement

Effect of 2-acrylamide-2-methylpropane sulfonic acid on the early strength enhancement of calcium silicate hydrate seed

Ensemble machine learning and Shapley additive explanations for the ability of C-S-H seeds to accelerate cement hydration

Tuning the Hydration Acceleration Efficiency of Calcium Carbonate by Pre-Seeding with Calcium Silicate Hydrate

Synthesis of C-S-H accelerating admixture and its effect on mechanical and hydration properties of engineering cementious composites

Synthesizing high-quality C-S-H seeds using the impinging stream precipitation method

Effect of Synthesis Conditions on Particle Size Morphology, Structure, and Acceleration Performance of C-A-S-H Nanoparticles