Axiomatic Mix Proportioning for Self-Compacting Concrete with Silica Fume
D. Annlin Jebitha,M. Ramesh Kannan
DOI: https://doi.org/10.1007/s40996-023-01050-9
2023-02-19
Abstract:This research focuses primarily on developing a comprehensive mix proportioning framework for Self-Compacting Concrete (SCC) with Silica Fume (SF). Initially, the mix proportioning of the blended concrete (SCC-SF) is perceived from literature using standard EFNARC guidelines. Using the discerned mix proportioning for SCC-SF, suitable concrete samples were prepared with varying quantities of concrete constituents, mineral admixtures, and different dosages of chemical admixtures, to interpret the fresh and hardened properties of the SCC-SF mixtures. The standard tests for fresh SCC such as L-box test, U-box, V-funnel test, and so on, were carried out for these blended mixtures. Furthermore, the compressive strength test for hardened SCC-SF concrete samples was performed. The experimental results of these fresh and hardened SCC-SF samples are incorporated into a machine learning methodology known as Decision Tree to get further insights on the functional requirements of the SCC-SF mixtures. Additionally, the inherent functional properties of SCC-SF are investigated through a novel mix proportioning methodology termed as Axiomatic Mix Proportioning (AMP) framework, which was developed based on an innovative systems design principle, known as Axiomatic Design. With AMP, the Functional Requirements (FRs) of SCC-SF such as workability, filling ability, passing ability, segregation resistance and compressive strength are investigated concerning its Design Parameters (DPs), i.e. constituents of SCC-SF. Ultimately, with the proposed AMP framework for SCC-SF, a comprehensive nomogram is developed to ease the mix proportioning of SCC-SF. From the nomogram, twenty-two optimal mix proportioning schema were generated. The optimal percentage of mineral admixture (SF), and dosage of chemical admixtures (Superplasticizer-SP, Viscosity Modifying Admixture-VMA, and Air-Entraining Admixture-AEA) to be used in SCC-SF to get maximum compressive strength (52 MPa) are 21.0 kg/m ( 6 % of cement by weight), 2.3 kg/m , 0.47 kg/m , and 1.97 kg/m , respectively. To validate the nomogram, additional twenty-two sets of SCC-SF samples were prepared, and fresh and hardened concrete tests were carried out. The test results of these additional twenty-two SCC-SF samples and the values of the corresponding sets in the nomogram perfectly correlate, and the percentage of deviations observed was very minimal.
engineering, civil