The role of post-annealing process on the physical, electrical and magnetic properties of nano-sized tin substituted Bi-2212 superconducting ceramics

Mehmet Ersin AYTEKİN
DOI: https://doi.org/10.1007/s10854-024-13631-z
2024-10-05
Journal of Materials Science Materials in Electronics
Abstract:In the present work, post-annealing was applied to Bi 2 Sr 1.80 (SnO 2 ) 0.2 Ca 2 Cu 1.75 Na 0.25 O y samples prepared by the solid state reaction method at different temperatures of 730 °C, 780 °C and 830 °C for fixed dwelling time. Samples were analysed by XRD, SEM, R-T and M-H measurements. In XRD results, it was determined that despite the decomposition of the Bi-2212 phase after the post-annealing, the major phase in all samples was Bi-2212 phase. In the SEM measurement results, plate-like grain formation was observed in the microstructures of all samples. With the increase of post-annealing temperature, the sizes of plate-like grains decreased due to the decomposition in the Bi-2212 superconducting phase. In R-T graphs, an increase in the Tc was obtained in the sample with 730 °C post-annealing. In the M-H plots of all samples, hysteresis loop was obtained as the characteristic behaviour of Bi-2212 high transition temperature superconductors. Jc values were calculated from Bean model. In the sample with 830 °C post-annealing, as a result of the development of flux pinning centres, 1.219 X 10 6 A/cm 2 of Jc value was obtained. Pinning Forces ( Fp ) were measured from Jc and B . In the sample with 830 °C post-annealing, the development of flux pinning mechanisms can be assisted by the secondary phases that arise from the decomposition of the Bi-2212 phase, leading to an increase in Fp .
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied
What problem does this paper attempt to address?