Enhancement of Bi-2223 Intergrain Connections by Heat Treatment Parameters Optimization
Shengnan Zhang,Botao Shao,Wen Zhang,Xiaobo Ma,Jixing Liu,Xueqian Liu,Jianqing Feng,Chengshan Li,Pingxiang Zhang
DOI: https://doi.org/10.1109/tasc.2022.3144126
IF: 1.9489
2022-01-01
IEEE Transactions on Applied Superconductivity
Abstract:Aiming at the improvement of current capacity in Bi 2 Sr 2 Ca 2 Cu 3 O 10+δ (Bi-2223) superconducting tapes, both the calcination process of precursor powders and the sintering process of Bi-2223 tapes have been modified to tune the intergrain connections. By adopting different calcination atmosphere of air and oxygen during the pre-calcination process, the phase composition of final precursor powder kept almost the same, while the particle size decreased in oxygen pre-calcinated powders, which thus led to the appearance of more secondary phases. On the other hand, due to the optimization of crystallization process of Bi-2223 phase, the microstructure with less pore density has been obtained, which proved that the increase of heating rate could obviously lead to the enhancement of intergrain connections of Bi-2223 tapes. Finally, critical current of 116 A has been achieved with the air pre-calcinated powders and 400 °C /h heating rate during HT2, which was ∼40% increase comparing with the I c of Bi-2223 tape with oxygen pre-calcinated powders and 100 °C/h heating rate in HT2 process.