PREPARATION OF Bi2Sr2Ca1Cu2Ox SUPERCONDUCTING FILMS ON Ag WIRES BY DIP-COATING METHOD

SONG Yang,ZHAO Liang,LI Pei,QU Timing,HAN Zhenghe,HUANG Yong

DOI: https://doi.org/10.3321/j.issn:0454-5648.2006.09.001

2006-01-01

Abstract:Bi2Sr2Ca1Cu2Ox (Bi–2212) thick films on Ag wires were prepared by using the dip-coating method. It was found that the partial melting temperature and solid phase sintering temperature parameters during heat treatment strongly influence the phase for- mation of Bi–2212. The critical current density of dip-coated thin wire with a diameter of 0.5 mm can reach 10 000 A/cm2 at liquid nitrogen temperature and at 0 T magnetic field. Post-annealing treatments at different temperatures and oxygen partial pressures were executed in order to study the variation of critical temperature (Tc) values. Results show that the optimal post-annealing temperature is 760 ℃, and the corresponding Tc value is 96.98 K. During the post-annealing process, the higher the oxygen partial pressure is, the higher the Tc value will be. Furthermore, the properties of Bi–2212 materials have time effects when exposed to air, causing their critical temperature to change.