Unveiling the Degradation Mechanism of High-Temperature Superconductor Bi2Sr2CaCu2O8+δ in Water-Bearing Environments
Yuan Huang,Lei Zhang,Xiaocheng Zhou,Lei Liao,Feng Jin,Xu Han,Tao Dong,Shuxiang Xu,Lin Zhao,Yunyun Dai,Qiuzhen Cheng,Xinyu Huang,Qingming Zhang,Lifen Wang,Nan-Lin Wang,Ming Yue,Xuedong Bai,Yafei Li,Qiong Wu,Hong-Jun Gao,Genda Gu,Yeliang Wang,Xing-Jiang Zhou
DOI: https://doi.org/10.1021/acsami.2c08997
IF: 9.5
2022-01-01
ACS Applied Materials & Interfaces
Abstract:The physical properties of copper oxide high-temperature superconductors have been studied extensively, such as the band structure and doping effects of Bi2Sr2CaCu2O8+delta (Bi-2212). However, some chemical-related properties of these superconductors are rarely reported, such as their stability in water-bearing environments. Herein, we report experiments combined with ab initio calculations that address the effects of water in contact with Bi-2212. The evolution of Bi-2212 flakes with exposure to water for different time intervals was tested and characterized by optical microscopy (OM), atomic force microscopy (AFM), Raman spectroscopy, transmission electron microscopy (TEM), and electrical measurements. The thickness of Bi-2212 flakes is gradually decreased in water, and some thin flakes can be completely etched away after a few days. The stability of Bi-2212 in other solvents is also evaluated, including alcohol, acetone, HCl, and KOH. The morphology of Bi-2212 flakes is relatively stable in organic solvents. However, the flakes are etched relatively quick in HCl and KOH, especially in an acidic environment. Our results imply that hydrogen ions are primarily responsible for the deterioration of their properties. Both TEM and calculation results demonstrate that the atoms in the Bi-O plane are relatively stable when compared to the inner atoms in Sr-O, Ca-O, and Cu-O planes. This work contributes toward understanding the chemical stability of a Bi-2212 superconducting device in environmental medium, which is important for both fundamental studies and practical applications of copper oxide high-temperature superconductors.