Refinement of Nanoporous Copper by Dealloying Al-Cu Alloy in NaOH Solution Containing Sodium Dodecyl Sulfate
Jie Li,Zhi-Bin Yi,Nuo-Tong Li,Na-Na Yu,Hao-Ran Geng,Zhibin Yi,Nana Yu,Haoran Geng
DOI: https://doi.org/10.1039/d3cp02373g
IF: 3.3
2023-07-05
Physical Chemistry Chemical Physics
Abstract:This work reports the refinement of nanoporous copper (NPC) ligaments by introducing sodium dodecyl sulfate (SDS) surfactant into dealloying process. Al80Cu20 (at.%) alloy precursor is chemically dealloyed in a mixed solution of NaOH and SDS surfactant, producing NPC with a hierarchical microstructure. The micron-scaled skeletons that build up the higher level networks consist of geometrically similar nano-scaled bi-continuous ligaments-pore networks at the lower level. It has been found that the size of the ligaments in the lower level networks reduces from ~32 nm to ~24 nm with increasing SDS concentration to 1 mM. Further increasing the SDS concentration to 5 mM only lead to a slight ligament size decrease to ~21 nm. Strikingly, nano-sized cones are formed on the lower level network surface in the case containing 1~mM SDS, and the cone numbers greatly rises when the SDS concentration increases to 5 mM. The surface diffusivity of Cu adatoms is evaluated based on the experimental data, and the refinement of the ligament as well as the formation of cones are associated with the decreased surface diffusivity and the retarded Cu adatoms motions with the addition of SDS. Quantum chemical calculation and molecule dynamic simulations are performed to model the adsorption behaviour of SDS. It has been revealed that SDS-substrate interaction increases with SDS molecule number before SDS reaches saturation.
chemistry, physical,physics, atomic, molecular & chemical