Abstract:The microstructure and hydrogen storage properties of Ti10+xV80-xFe6Zr4 (x = 0, 5, 10, 15) alloys have been studied. XRD and SEM analyses show that all alloys consist of a BCC main phase and a small fraction of C14 Laves secondary phase, in which the latter precipitates along the grain boundary of the former becoming network structure. With increasing Ti content in the alloy, the lattice parameter and cell volume of the BCC main phase of the alloy increase. The chemical composition of each phase is analysed by EDS, from which the lattice parameters of BCC phase have a good linear relationship with their average atomic radii. All bulk alloys have good activation behaviors and hydriding kinetics. With the increase of Ti content, the incubation time for activation decreases first and then increases under an initial hydrogen pressure of 4 MPa at 298 K. The incubation time of Ti15V75Fe6Zr4 alloy is only 12 s. It is one of the shortest incubation time in V-based solid solution alloys as far as we know, which may be related to the existence of C14 Laves phase. All the alloys have relatively high hydrogen absorption capacities of above 3 wt%, which increase first and then decrease as the Ti content increases, achieving the maximum capacity of 3.61 wt% at x = 10 at 298 K. With increasing x, the equilibrium plateau pressure of dehydrogenation of the samples at 353 K decreases owing to the expansion of unit cell of main phase, which is far below 0.1 MPa for x = 10 and 15. The maximum desorption capacity of 1.94 wt% (desorbed to 0.001 MPa) is obtained at x = 5, compared to that of 1.6 wt% (desorbed to 0.1 MPa) achieved at x = 0.

Superior reversible hydrogen storage capacity of V-based solid solution alloy above atmospheric pressure with yttrium substitution

Study on the modification of Zr-Mn-V based alloys for hydrogen isotopes storage and delivery

Highly Efficient Hydrogen Storage Capacity of 2.5 wt % Above 0.1 MPa Using Y and Cr Codoped V-Based Alloys

Microstructure and hydrogen storage properties of Ti1.0VxMn2-x(x=0.6-1.6) alloys

Microstructure and hydrogen storage properties of Ti1.0VxMn2-x(x=0.6 similar to 1.6) alloys

Microstructure and hydrogen storage properties of Ti10+xV80-xFe6Zr4 (x=0~15) alloys

Hydrogen storage properties of V+TiFe0.85Mn0.15 multi-phase alloys

Hydrogen Storage Properties of Ti-Cr-Mn-M (M=V, Fe, Ni, Cu) Alloys

Phase structures and hydrogen storage properties

Hydrogen storage capabilities of the alloys Fe 0.85Mn 0.15Ti 0.9M 0.1 (M=Zr, V, Ca)

Phase Structures and Hydrogen Storage Properties of TiV1.35Cr1.35-xMnx Alloys(x=0～0.45)

Hydrogen storage properties of TiMn2-based alloys

Microstructures and Hydrogen Storage Properties of Ti10V83-xFe6ZrMnx Alloys

Reversible Hydrogenation of AB2-type Zr–Mg–Ni–V Based Hydrogen Storage Alloys

Hydrogen Storage Characteristics of TiMn1.25-5yCr0.25(V4Fe)y Alloys

Hydrogen storage in Ti–V-based body-centered-cubic phase alloys

The Effects of Partial Substitution of Mn by Cr on the Phase Structure, Microstructure and Electrochemical Properties of Ti-Zr-V-Mn-Ni Hydrogen Storage Alloys

Effects of Y Substitution for Ti on the Microstructure and Electrochemical Properties of Ti-V-Fe-Based Hydrogen Storage Alloys

Experimental and theoretical insights into vanadium-based alloys for room temperature hydrogen storage on the example of Ti16Cr22Zr5V55-Fe2Mn (x=0–3) alloys

Enhancement of vanadium addition on hydrogen storage properties of high entropy alloys TiZrFeMnCrV x

High Pressure Solidification of Alloying Substitution and Promotion of Hydrogen Storage Properties in AB2-type Y-Zr-Ti-Fe Based Alloys