Abstract:The microstructure and hydrogen storage properties of Ti10+xV80-xFe6Zr4 (x = 0, 5, 10, 15) alloys have been studied. XRD and SEM analyses show that all alloys consist of a BCC main phase and a small fraction of C14 Laves secondary phase, in which the latter precipitates along the grain boundary of the former becoming network structure. With increasing Ti content in the alloy, the lattice parameter and cell volume of the BCC main phase of the alloy increase. The chemical composition of each phase is analysed by EDS, from which the lattice parameters of BCC phase have a good linear relationship with their average atomic radii. All bulk alloys have good activation behaviors and hydriding kinetics. With the increase of Ti content, the incubation time for activation decreases first and then increases under an initial hydrogen pressure of 4 MPa at 298 K. The incubation time of Ti15V75Fe6Zr4 alloy is only 12 s. It is one of the shortest incubation time in V-based solid solution alloys as far as we know, which may be related to the existence of C14 Laves phase. All the alloys have relatively high hydrogen absorption capacities of above 3 wt%, which increase first and then decrease as the Ti content increases, achieving the maximum capacity of 3.61 wt% at x = 10 at 298 K. With increasing x, the equilibrium plateau pressure of dehydrogenation of the samples at 353 K decreases owing to the expansion of unit cell of main phase, which is far below 0.1 MPa for x = 10 and 15. The maximum desorption capacity of 1.94 wt% (desorbed to 0.001 MPa) is obtained at x = 5, compared to that of 1.6 wt% (desorbed to 0.1 MPa) achieved at x = 0.

High Pressure Solidification of Alloying Substitution and Promotion of Hydrogen Storage Properties in AB2-type Y-Zr-Ti-Fe Based Alloys

Development of Ti–Zr–Mn–Cr-(V–Fe) Based Alloys for Hydrogen Feeding System in Hydrogen Metallurgy Application

Binding Energy Crossover Mechanism Enables Low-Temperature Hydrogen Storage Performance of Dual-Phase TiZrCrMnNi(VFe) High-Entropy Alloy

Experimental and Theoretical Investigation on the Enhanced Hydrogen Storage Performance of Ti–Cr–Mn–Fe-Based Alloys Modified by Nb Substitution

Influence of Fe Content on the Microstructure and Hydrogen Storage Properties of Ti16Zr5Cr22V57−xFex (x = 2–8) Alloys

Microstructure and hydrogen storage properties of Ti10V84-xFe6Zrx (x = 1-8) alloys

Phase Structure and Hydrogen Storage Properties of Ti17cr23v55-Xzr5fex (X=11 Similar to 16) Alloys

Exploration of Ti substitution in AB2-type Y Zr Fe based hydrogen storage alloys

Achieving Superior De-/Hydrogenation Properties of C15 Laves Phase Y-Fe-Al Alloys by A-side Substitution

Microstructure and hydrogen storage properties of Ti10+xV80-xFe6Zr4 (x=0~15) alloys

Hydrogen storage alloys for high-pressure suprapure hydrogen compressor

Hydrogen storage capabilities of the alloys Fe 0.85Mn 0.15Ti 0.9M 0.1 (M=Zr, V, Ca)

Hydrogen storage properties of TiMn2-based alloys

High-pressure hydrogen storage performances of ZrFe<sub>2</sub> based alloys with Mn, Ti, and V addition

Crystal structure and hydrogen storage properties of AB-type TiZrNbCrFeNi high-entropy alloy

Enhanced Hydrogen Storage Properties of ZrTiVAl1-xFex High-Entropy Alloys by Modifying the Fe Content

Development of (Ti–Zr) 1.02 (Cr–Mn–Fe) 2 -Based Alloys toward Excellent Hydrogen Compression Performance in Water-Bath Environments

Optimized Hydrogen Storage Properties of Ti-Zr-Mn-VFe-based Alloys by Orthogonal Experiment for Upscaled Production

Tuning hydrogen storage thermodynamic properties of ZrFe2 by partial substitution with rare earth element Y

Study on hydrogen storage property of (ZrTiVFe) Al high-entropy alloys by modifying Al content

Study on microstructure and the hydrogen storage behavior of a TiVZrNbFe high-entropy alloy