Formation of Mo2C in molybdenum tubing inside a graphite furnace filled with pure nitrogen at high temperature

Lin Yang,Tongguang Zhai,Yan Jin,Todd Leonhardt,Wenfang Li
DOI: https://doi.org/10.1016/j.ijrmhm.2021.105489
IF: 4.804
2021-04-01
International Journal of Refractory Metals and Hard Materials
Abstract:<p>Pure Mo tubing (0.381 mm in thickness) were annealed at 1700 °C for 4 h in a graphite furnace filled with pure N<sub>2</sub> (99.995%) to evaluate the feasibility of employing the Mo tubing for high temperature thermocouple sheath. It was found that the Mo tubes were shattered after several cycles of annealing treatment. EBSD measurements revealed that the fractured Mo tubing was transformed almost completely into Mo<sub>2</sub>C 99.4% in volume fraction. The Mo<sub>2</sub>C phase had a "zebra" eutectic structure, consisting of 83.25% of orthorhombic Mo<sub>2</sub>C (Orth.) and 16.15% of hexagonal Mo<sub>2</sub>C (Hex.). This indicated that the carbon from the heating elements in the furnace somehow reacted with the Mo tubing to form Mo<sub>2</sub>C without direct physical contact between them in N<sub>2</sub> at 1700 °C. Thermodynamic analysis supported the hypothesis that N<sub>2</sub> gas served as an intermedium transporting the C from the heating elements to the Mo tubes by first reacting with the C to produce a cyanogen (C<sub>2</sub>N<sub>2</sub>) gas which subsequently reacted with Mo to form Mo<sub>2</sub>C at 1700 °C in the graphite furnace. The O<sub>2</sub> effect on the Mo<sub>2</sub>C formation was also analyzed, suggesting it was negligible because of the scarcity of oxygen in the pure N<sub>2</sub> gas in the furnace. No Mo nitride could be formed in the Mo tube since N<sub>2</sub> energetically prefers to react to C first at 1700 °C in the furnace.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?