Synthesis and Characterization of 2D Molybdenum Carbide (MXene)
Joseph Halim,Sankalp Kota,Maria R. Lukatskaya,Michael Naguib,Meng-Qiang Zhao,Eun Ju Moon,Jeremy Pitock,Jagjit Nanda,Steven J. May,Yury Gogotsi,Michel W. Barsoum
DOI: https://doi.org/10.1002/adfm.201505328
IF: 19
2016-02-17
Advanced Functional Materials
Abstract:Large scale synthesis and delamination of 2D Mo 2 CT x (where T is a surface termination group) has been achieved by selectively etching gallium from the recently discovered nanolaminated, ternary transition metal carbide Mo 2 Ga 2 C. Different synthesis and delamination routes result in different flake morphologies. The resistivity of free‐standing Mo 2 CT x films increases by an order of magnitude as the temperature is reduced from 300 to 10 K, suggesting semiconductor‐like behavior of this MXene, in contrast to Ti 3 C 2 T x which exhibits metallic behavior. At 10 K, the magnetoresistance is positive. Additionally, changes in electronic transport are observed upon annealing of the films. When 2 μm thick films are tested as electrodes in supercapacitors, capacitances as high as 700 F cm −3 in a 1 m sulfuric acid electrolyte and high capacity retention for at least 10,000 cycles at 10 A g −1 are obtained. Free‐standing Mo 2 CT x films, with ≈8 wt% carbon nanotubes, perform well when tested as an electrode material for Li‐ions, especially at high rates. At 20 and 131 C cycling rates, stable reversible capacities of 250 and 76 mAh g −1 , respectively, are achieved for over 1000 cycles.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology