Abstract:In this paper, we discussed recent studies done in our laboratories with a floating catalyst chemical vapor deposition (CVD) method. We can grow single- or double-walled carbon nanotubes (SWNTs/DWNTs) with different kinds of catalysts. Single-walled carbon nanotubes without amorphous carbon coating were prepared by thermally decomposing acetylene (C2H2) at the temperature range of 750–1200°C with ferrocene as catalyst. While with sulfur promoted ferrocene catalyst, double-walled carbon nanotubes were mass-produced by pyrolizing C2H2 at the temperature range of 900–1100°C. Furthermore, tunable growth of DWNTs with different diameter was achieved in our experiment. It is found that DWNTs produced at lower carbon partial pressure have much smaller inner tubes, even DWNTs with the smallest inner diameter of 0.4nm was found in here. As convenient and effective tool, radial breathing mode (RBM) of Raman scattering technique can be used to distinguish SWNTs from DWNTs. In further studies of Raman scattering with DWNTs, the possible match of the inner tubes and the outer tubes according to the RBM bands was assigned, and different chirality types were discussed according to the diameter and chirality dependence of resonant Raman vibration. We also investigated the temperature-dependent frequency shift of resonant Raman spectra of DWNTs in the range of 78–650K. We found that different RBM peaks, which are relative to different tube diameters, have different temperature coefficient of frequency shift, and the larger diameter carbon nanotubes have more RBM frequency downshift with increasing temperature. It is ascribed to the RBM frequency variation to the temperature dependence of the stretching force constant of C–C bond. Besides, Polarized Raman spectra were preformed on well-aligned SWNTs structure fabricated through post-growth method and found that the angular dependence of Raman intensity is consistent well with the predictions of the resonance Raman theory.

High Temperature Treatment and Characterization of Carbon Nanotubes

99.9% Purity Multi-Walled Carbon Nanotubes by Vacuum High-Temperature Annealing

Study of Controlled Growth of Carbon Nanotubes in Microstructures at Low Temperature

Purifying Double-Walled Carbon Nanotubes by Vacuum High-Temperature Treatment

A Treatment Method to Give Separated Multi-Walled Carbon Nanotubes with High Purity, High Crystallization and a Large Aspect Ratio

The effect of high-temperature annealing on the structure and electrical properties of well-aligned carbon nanotubes

Temperature Selective Growth Of Carbon Nanotubes By Chemical Vapor Deposition

Crystallization Behavior of the Amorphous Carbon Nanotubes Prepared by the CVD Method

Influence of Heat Treatment on Field Emissive Properties of Single-Walled Carbon Nanotubes

Effect of Graphitizing Treatment on Structure of Carbon Nanotubes

Growth Of High-Quality Single-Wall Carbon Nanotubes Without Amorphous Carbon Formation

High-strength carbon nanotube fibers with near 100% purity acquired via isothermal vacuum annealing

Mass Spectrum of Residual Gas on Single-Walled Carbon Nanotubes and W Tip During Heat Treatment

How Single-Walled Carbon Nanotubes are Transformed into Multiwalled Carbon Nanotubes during Heat Treatment

Thermal Stability of Carbon Nanotubes Probed by Anchored Tungsten Nanoparticles

Purification of Single-Wall Carbon Nanotubes

Controllable preparation and properties of single-/double-walled carbon nanotubes

Thermal Stability of Carbon Nanotubes under 5.5Gpa

Large‐Scale Synthesis, Annealing, Purification, and Magnetic Properties of Crystalline Helical Carbon Nanotubes with Symmetrical Structures

Hydrothermal treatment to prepare hydroxyl group modified multi-walled carbon nanotubes

Mechanism of Carbon Nanotube Growth in a Nano-agglomerate Fluidized Bed