Abstract:In a typical FCCVD process, the purity of the initial product grown by the standard process was more than 90 wt%, with a yield of 0.5 g/h. The average G/D ratio of the initial product was 178, and it had a distinct RBM peak. HRTEM confirmed that the synthesized SWCNTs had high purity and crystallinity. Carbon nanotubes (CNTs) were synthesized by floating catalyst chemical vapor deposition (FCCVD) reactions. The complicated processing parameters that included a precursor solution composition, reaction temperature, flow rate of the carrier gas, weak oxidants, and injection rate of the precursor solution were controlled to synthesize single‐walled carbon nanotubes (SWCNTs) during the reaction process. The effects of the processing parameters were analyzed with respect to the formation of SWCNTs, yield, and the crystallinity in the CNTs structure. The SWCNTs were characterized by the Raman spectroscopy, scanning electron microscope, high‐resolution transmission electron microscopy, and thermogravimetric analysis. A high reaction temperature, high H2 flow rate, low injection rate of solution precursor, and low concentrations of iron catalysts in the reaction were important factors to improve the crystalline quality of the SWCNTs. The purity of the initial product grown by the standard process was more than 90 wt %, with a yield of 0.5 g/h. The average G/D ratio of the initial product was 178, and it had a distinct RBM peak. HRTEM confirmed that the synthesized SWCNTs had high purity and crystallinity. The SWCNTs could be tunable to meet a particular application by varying the reaction conditions.

Crystallization Behavior of the Amorphous Carbon Nanotubes Prepared by the CVD Method

Supercooling Behaviour and Non-Isothermal Crystallization Processes of Aqueous Suspensions of Carbon Nanotubes

In Situ Fabrication and Graphitization of Amorphous Carbon Nanowires and Their Electrical Properties

Growth Of High-Quality Single-Wall Carbon Nanotubes Without Amorphous Carbon Formation

Study of Controlled Growth of Carbon Nanotubes in Microstructures at Low Temperature

High Temperature Treatment and Characterization of Carbon Nanotubes

Crystallization and Raman Shift of Array-Orderly Silicon Nanowires after Annealing at High Temperature

Amorphization and Directional Crystallization of Metals Confined in Carbon Nanotubes Investigated by in Situ Transmission Electron Microscopy

Catalyst-Free in Situ Carbon Nanotube Growth in Confined Space Via High Temperature Gradient

Annealing amorphous carbon nanotubes for their application in hydrogen storage

Temperature Selective Growth Of Carbon Nanotubes By Chemical Vapor Deposition

Effect of Graphitizing Treatment on Structure of Carbon Nanotubes

Graphitization Behavior of Carbon Nanofibers Prepared by the Floating Catalyst Method

Ultrahigh Convergent Thermal Conductivity of Carbon Nanotubes from Comprehensive Atomistic Modeling

Template-confined growth and structural characterization of amorphous carbon nanotubes

The effect of high-temperature annealing on the structure and electrical properties of well-aligned carbon nanotubes

Crystallization and Phase Transition of Titanium Oxide Nanotube Arrays

A Treatment Method to Give Separated Multi-Walled Carbon Nanotubes with High Purity, High Crystallization and a Large Aspect Ratio

Quantitative Evidence for the Dependence of Highly Crystalline Single Wall Carbon Nanotube Synthesis on the Growth Method

Controlling the Crystalline Quality and Yield of Single‐Walled Carbon Nanotubes via Floating Catalyst Chemical Vapor Deposition Synthesis

Formation of metallic nano-crystals from gel-like precursor films for CVD nanotube growth: An in-situ TEM characterization