Abstract:Single-walled carbon nanotubes (SWNTs) have attracted much attention due to their unique structural, mechanical, chemical, and electrical properties. Catalytic chemical vapor deposition (CCVD) through decomposition of hydrocarbons is one of the most challenging synthesis methods to produce SWNTs in large scale. In this paper, high quality SWNTs prepared in a nano-agglomerated fluidized bed reactor (NAFBR) was reported. The reactor is a vertical quartz tube with the inner diameter of about 50 mm. Catalysts nanoparticles used for the production of SWNTs were prepared with Fe metal nanoparticles carried on the surface of MgO. About 150g catalysts powders were loaded on the gas distribution grid. The reaction temperature was controlled at not less than 1123 K. The carrier gas of argon was used to maintain turbulent fluidization of the catalysts powders in FBR. The hydrogen gas was used to reduce the catalysts and to synergize the growth of SWNTs with methane. The powder products were spherical agglomerates of SWNTs bundles tangling with the catalysts particles. By optimizing the process parameters of CCVD, the products of SWNTs with the diameter about 0.9 ∼ 1.8 nm were prepared, without any multi-walled carbon nanotubes (MWNTs) or amorphous carbon. The microstructure of SWNTs products were characterized by the methods of high resolution transmission electron microscopy (HRTEM), scanning electron microscopy (SEM), Raman spectra, etc. The NAFBR is a commercially viable (effective and continuous production at a low cost) process for the production of SWNTs.

Mechanism of Carbon Nanotube Growth in a Nano-agglomerate Fluidized Bed

The Large-Scale Production of Carbon Nanotubes in A Nano-Agglomerate Fluidized-Bed Reactor

Production of Carbon Nanotubes in A Packed Bed and A Fluidized Bed

Agglomerated CNTs Synthesized in a Fluidized Bed Reactor: Agglomerate Structure and Formation Mechanism

Study of Controlled Growth of Carbon Nanotubes in Microstructures at Low Temperature

Catalysts effect on morphology of carbon nanotubes prepared by catalytic chemical vapor deposition in a nano-agglomerate bed

The Mass Production of Carbon Nanotubes Using a Nano-Agglomerate Fluidized Bed Reactor: A Multiscale Space–time Analysis

Agglomerated carbon nanotubes and its mass production in a fluidized-bed reactor

Fluidization characteristics, solids distributions and gas mixing of a carbon nanotube agglomerate fluidized bed

Hydrodynamics and Gas Mixing in A Carbon Nanotube Agglomerate Fluidized Bed

Effect of Catalyst on Morphology of Carbon Nano-Materials Prepared in A Nano-Agglomerate Bed

Mass Production of Aligned Carbon Nanotube Arrays by Fluidized Bed Catalytic Chemical Vapor Deposition

On-line intermittent growth of carbon nanotubes in a self-made tapered fluidized bed reactor at different inlet distances

TEM Investigation on the Growth Mechanism of Carbon Nanotubes Synthesized by Hot-Filament Chemical Vapor Deposition.

Catalyst-Free in Situ Carbon Nanotube Growth in Confined Space Via High Temperature Gradient

Growth of Branch Carbon Nanotubes on Carbon Nanotubes As Support

In situ growth of CNTs on carbon fiber by chemical vapor deposition

Production of High Quality Single-Walled Carbon Nanotubes in a Nano-Agglomerated Fluidized Bed Reactor

Synthesis of Single-Walled Carbon Nanotubes by Chemical Vapor Deposition of Methane in A Fluidized Bed Reactor: Temperature and Reaction Time Effects

Temperature Selective Growth Of Carbon Nanotubes By Chemical Vapor Deposition

Buliding microstructures of organized carbon nanotubes by chemical vapor deposition