Abstract:High-entropy alloys (HEAs) of AlxCoCrFeNi (x = 0.2, 0.5, and 1) were created using the spark plasma sintering (SPS) method in conjunction with an aerosolized powder. Their microstructure and phase constituents were characterized by X-ray diffractometry, scanning electron microscopy, and projection electron microscopy. The tensile properties, hardness, compactness, and damping properties were also tested. The results showed that the crystal structure of AlxCoCrFeNi HEAs changed significantly with the Al content, from the original single face-centered cubic FCC phase (Al0.2CoCrFeNi) to an FCC + BCC + B2 structure (Al0.5CoCrFeNi), and then to FCC + BCC + B2 + Sigma (σ) phase structures (AlCoCrFeNi). Twin crystals with FCC structure were also observed in the TEM of AlCoCrFeNi. A chemical composition analysis showed that the crystal structure transformation was related to the segregation caused by the increase of Al element content. The hardness of the AlxCoCrFeNi HEAs increased with the Al content, and the hardness of AlCoCrFeNi reached the highest value of 585.4 HV. The tensile properties of the alloy showed a trend of increasing and then decreasing values with the increase in Al content. The yield strength, ultimate tensile strength, and elongation of the Al0.5CoCrFeNi alloy reached the highest values of 557.7 MPa, 954.4 MPa, and 32.2%, respectively. Moreover, the fracture mechanism of the Al0.2CoCrFeNi and Al0.5CoCrFeNi alloys was that of a typical ductile fracture, while for the AlCoCrFeNi alloy, it was that of a cleavage fracture. The compactness of the alloy increased with the Al content. The combination of the FCC + BCC + B2 phase resulted in the damping capacity of Al0.5CoCrFeNi alloy reaching 0.018 at the corresponding strain amplitude of 6 × 10−4.

Enhancement of Mechanical Properties and Corrosion Resistance of Ultra-Fine Grain Al0.4FeCrCo1.5NiTi0.3 High-Entropy Alloy by MA and SPS Technologies

Microstructure and mechanical properties of CoCrFeNiTa high entropy alloy prepared by mechanical alloying and spark plasma sintering

Enhancing the Strength of AlCrFeNi HEAs Via Tailoring Aluminum Content and Optimal Aging Treatment

Microstructure and Properties of NiCoCrAlTi High Entropy Alloy Prepared Using MA-SPS Technique

Enhancement of strength–ductility combination and corrosion resistance behaviour in (FeCoNiCr) 92 Ti 3.5 Al 4.5 high-entropy alloy

Microstructure, mechanical properties and corrosion resistance of an as-cast fine-structured Cr-Fe-Ni-Al-Si high entropy alloy

Microstructure and Magnetic Characteristics of AlCrCuFeNiTi High-Entropy Alloy Prepared by Mechanical Alloying Followed by Spark Plasma Sintering

Microstructure, Mechanical Properties, and Damping Capacity of AlxCoCrFeNi High-Entropy Alloys Prepared by Spark Plasma Sintering

Microstructural evolution, mechanical and corrosion behavior of an Al7.5Co20.5Fe24Ni24Cr24 high‐entropy alloy

Structure and properties of Fe40Mn20Cr20Ti10Al10 high-entropy alloy fabricated by mechanical alloying and spark plasma sintering

Microstructure, mechanical properties and corrosion resistance of an as-cast fine-structure Cr-Fe-Ni-Al-Si high entropy alloy with Mo addition

An important improvement of strength and ductility on a new type of CoCr2.5FeNi2TiW0.5 high entropy alloys under two different protective gases by selective laser melting

Nanostructured Al–Ti–Fe–Mn–Ni High-Entropy Alloy by Mechanical Alloying: Synthesis and Characterization

Microstructure and mechanical properties of Al-Fe-Co-Cr-Ni high entropy alloy fabricated via powder extrusion

Microstructure and mechanical properties of CrFeNi high-entropy alloy reinforced by Al and Ti elements

Synthesis and Characterization Study of Al10Cr25Co20Ni25Fe20 High-Entropy Alloy Powders through Mechanical Alloying

Microstructural evolution and mechanical properties of novel nanoparticles strengthened CoCrFeNi based high entropy alloy

Magnetic and mechanical properties of nanotwin SiO 2 -FeCoNi(AlSi) 0.4 high entropy alloy prepared by mechanical alloying and spark plasma sintering

Microstructure, Mechanical and Corrosion Properties of Co- and Cu-free AlxCrFeNi2.5Mo1-x High Entropy Alloys

Synthesis and Phase Evolution of a Nanocrystalline FexCrNiAl (x = 1.0, 0.5, 0.25) High-Entropy Alloys by Mechanical Alloying

Enhanced Strength and Ductility in a Spark Plasma Sintered CoCrCu0·5NiAl0.5 High-Entropy Alloy Via a Double-Step Ball Milling Approach for Processing Powders