Abstract:Aluminum hydride (AlH3) exhibits attractive properties, such as high hydrogen/energy storage, relatively good stability, and low dehydrogenation temperature. Thus, AlH3 has appreciable prospects as a component in solid propellant for promoting the specific impulse of rocket engines and for effectively reducing the erosion of engine nozzles. The TG-MS, SEM, XRD, XPS, and EDS results show that the thermal reaction of AlH3 is divided into three stages: (1) Dehydrogenation (below 210 °C, 2AlH3→2Al+3H2) starts from the inherent defects on the surface with an incomplete decomposition due to the passivation reaction in which an amorphous Al2O3 layer is formed to encapsulate the contained hydrogen. This is accompanied by nucleation and growth of Al nuclei from the outer particles to the inner particles and the formation of H2O via oxidation of the generated hydrogen. (2) The primary oxidation of Al (210–650 °C, 4Al+3O2→2γ-Al2O3) is attributed to a discontinuous layer of γ-Al2O3, which is transformed from amorphous Al2O3 that results in the reaction of naked residual Al and O2. (3) The secondary oxidation of residual Al (above 650 °C, 4Al+3O2→2α-Al2O3) occurs because of the crystal conversion from γ-Al2O3 to α-Al2O3, which leads to the shrinkage of the oxide shell and to the formation of cracks. Also, melting of residual Al breaks the shell, and this induces further oxidation. The results obtained for the microscopic kinetics mechanisms of dehydrogenation and oxidation of AlH3, show a clear direction for research regarding modifications of AlH3 as the theoretical foundation and are beneficial for the wide use of AlH3 in applications such as solid propellant as an energetic material and as a hydrogen source for fuel cells.

Stability, reactivity and decomposition kinetics of surface passivated α-AlH3 crystals

Surface Passivation of Aluminum Hydride Particles Via Atomic Layer Deposition

Enhanced stability and combustion performance of AlH3 in combination with commonly used oxidizers

Advanced preparation and processing techniques for high energy fuel AlH3

AlH3 As High-Energy Fuels for Solid Propellants: Synthesis, Thermodynamics, Kinetics, and Stabilization

Study on dehydrogenation and oxidation kinetics mechanisms of micron α-AlH3 in an oxidative atmosphere

Effect of AlH 3 on the Energy Performance and Combustion Agglomeration Characteristics of Solid Propellants

Thermal Reaction and Combustion Mechanism of AlH3 with Different Particle Sizes

Reactivity and stabilization mechanisms of AlH3 crystals by coating of polyvinylidene difluoride

Theoretical study on the stability mechanism of a high energy system composed of molecules containing COC or –N3 groups and aluminum hydride

Thermal Oxidation and Heterogeneous Combustion of AlH3 and Al: A Comparative Study

Wet Chemical Synthesis of Non-solvated Rod-Like Α'-Alh3 As a Hydrogen Storage Material.

Ultra-fast response behavior of aluminum hydride (AlH3) in a quasi-detonation environment

Directed Stabilization by Air-Milling and Catalyzed Decomposition by Layered Titanium Carbide Toward Low-Temperature and High-Capacity Hydrogen Storage of Aluminum Hydride

Dehydriding properties of γ-AlH3

Enhanced Thermal Stability and High-Quality of Α-Alh3 Via Crystal Seed Preparation Method

Hydrogen Desorption Behaviors of Γ-Alh 3 : Diverse Decomposition Mechanisms for the Outer Layer and the Inner Part of Γ-Alh 3 Particle

Improved Hydrogen Generation from the Hydrolysis of Aluminum Ball Milled with Hydride

The enhanced thermal stability and reduced hygroscopicity of aluminum hydride coated with vinyltrimethoxysilane

Effects of AlH 3 particle size and loading on the combustion and agglomeration of solid propellants

Catalytically ultrathin titania coating to enhance energy storage and release of aluminum hydride via atomic layer deposition