Abstract:In the processing of porous ceramics, shrinkage from green body to sintered compact during drying and sintering is one of key concerns which affect microstructure and properties of the porous ceramics. Through releasing gases from the burning of the pore forming agents and volume expansion from formation of low density resultants during sintering, the sintering shrinkage can be effectively compensated and near net size preparation can be achieved. Herein, near net size porous alumina‐calcium aluminate ceramics with controllable shrinkage have been prepared by a combination of gelcasting and pore‐forming agent process through adjusting the amount of CaCO3 and polymethyl methacrylate (PMMA) microspheres added. Al2O3 and CaCO3 were used as raw material, polymethyl methacrylate (PMMA) microspheres were used as pore‐forming agent, isobutylene/maleic anhydride copolymer (Isobam104) was used as gelling agent and dispersing agent. The effects of the addition amounts of CaCO3 and PMMA in the slurry on the phase composition, shrinkage, porosity, and strength of porous alumina‐calcium aluminate ceramics were investigated. The results show that as the CaCO3 addition amount increases from 0 wt% to 20 wt%, the shrinkage of the samples gradually decreases from 7.3 % to ‐1.4 %, and the consequent porosity increases from 58 % to 66 %, while the compressive strength increases from 5.9 MPa to 15.5 MPa. When PMMA content increases from 10 wt% to 50 wt%, the shrinkage of the samples decreases first and then increases, the porosity increases from 51 % to 74 %, and the compressive strength decreases from 12.5 MPa to 5.3 MPa. The mechanisms for controlling of shrinkages during preparation of porous alumina‐calcium aluminate ceramics can be attributed to the following aspects: on one hand, gases release from burning of PMMA and decomposition of CaCO3 during sintering; on the other hand, volume expansion due to formation lower density calcium aluminates which come from the reactions between CaO and Al2O3. Near net size preparation technique is of great significance for the manufacture of porous ceramics since the subsequent machining cost can be effectively reduced.

Non-shrinkage porous ceramics by In-situ hollow sphere method based on the Kirkendall effect of Al particle

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

Hierarchical porous MgAl2O4 ceramic in‐situ structured by hollow particles: Low‐shrinkage and High‐strength

A New Al 2 O 3 Porous Ceramic Prepared by Addition of Hollow Spheres

Near-zero-shrinkage Al2O3 ceramic foams with coral-like and hollow-sphere structures via selective laser sintering and reaction bonding

A Novel Way to Prepare Hollow Sphere Ceramics

A Novel Process to High‐strength and Controlled‐shrinkage Al2O3 Foams with Open‐cell by Al Powder Hollowing Technology

Near Net Size Sintering of Porous Cordierite Ceramics with Excellent Properties

Porous Alumina-Bentonite Ceramics: Effects of Fillers and Molding Technique

Study of the effect of the morphology of initial powders on the structural and dimensional characteristics of SiC-based porous ceramic materials

New approach to preparing near zero shrinkage alumina ceramic cores with excellent properties by vat photopolymerization

Preparation of near net size porous alumina‐calcium aluminate ceramics by gelcasting‐pore‐forming agent processs

Low sintering shrinkage and high strength of porous mullite–zirconia ceramics: Effect of AlF3 and ZrSi2 contents

Effect of Burying Sintering on the Properties of Ceramic Cores Via 3D Printing

Porous Silica Ceramics with Uniform Pores from the In-Situ Foaming Process of Silica Poly-Hollow Microspheres in Inert Atmosphere

Direct ink writing additive manufacturing of porous alumina-based ceramic cores modified with nanosized MgO

Fabrication of Porous Al2TiO5-Al2O3 Ceramics Using Al2O3 Hollow Spheres Coated with TiO2 Sol

Porous ceramics with near‐zero shrinkage and low thermal conductivity from hazardous secondary aluminum dross

Preparation of low-shrinkage and high-performance alumina ceramics via incorporation of pre-sintered alumina powder based on Isobam gelcasting

Si3N4 Hollow Microsphere Toughened Porous Ceramics from Direct Coagulation Method Via Dispersant Reaction

Effect of Holding Time During Sintering on Microstructure and Properties of 3D Printed Alumina Ceramics