Abstract:As a substitute for conventional polymers for the preparation of biodegradable microcellular polymeric foams, polybutylene succinate (PBS) presents one of the most promising alternatives. However, the low melt strength of PBS makes it difficult to produce high-performance microcellular foams. This study aimed to improve the melt strength of PBS and explore the mechanical, thermal, crystalline, rheological, and supercritical CO2 foaming properties of PBS nanocomposites by using carbon nanofibers (CNFs). This study found that nanocomposites containing 7 wt% CNF exhibited the highest tensile strength, Young's modulus, and bending strength. Moreover, the CNF nanofillers were well dispersed in the PBS matrix without significant agglomeration, even at high filler concentrations. Furthermore, the nanocomposites demonstrated improved melting temperature and crystallinity compared with pure PBS. The rheological analysis showed that the addition of CNFs significantly increased PBS viscosity at low frequencies due to the interaction between the PBS molecular chains and CNFs and the entanglement of CNFs, resulting in a more complete physical network formation when the CNF content reached above 3 wt%. During the supercritical CO2 foaming process, the addition of CNFs resulted in increased cell density, smaller cells, and thicker cell walls, with good laps formed between the fibers on the cell walls of nanocomposite foams. Moreover, the electrical conductivity and electromagnetic interference (EMI) shielding properties of the foamed material were studied, and a nanocomposite foam containing 7 wt% CNF showed good electrical conductivity (4.5 × 10−3 S/m) and specific EMI shielding effectiveness (EMI SE) (34.7 dB/g·cm−1). Additionally, the nanocomposite foam with 7 wt% CNF also exhibited good compression properties (21.7 MPa). Overall, this work has successfully developed a high-performance, multifunctional PBS-based nanocomposite foam, making it suitable for applications in various fields.

Adsorption characteristics of amphiphilic open-cell poly(butylene succinate) foams with ultrahigh porosity

Mechanical and thermal properties of poly(butylene succinate)/plant fiber biodegradable composite

Study on the Foaming Behaviors of PBS and its Modification with PA6IcoT Assisted by scCO2

Multiporous Microstructure for Enhancing the Water Absorption and Swelling Rate in Poly(sodium Acrylic Acid) Superabsorbent Hydrogels Based on a Novel Physical and Chemical Composite Foaming System

Preparation of Enhanced Poly(Butylene Succinate) Foams

Engineering of Polybutylene Succinate with Long-Chain Branching Toward High Foamability and Degradation

The Essential Role of PBS on PBAT Foaming under Supercritical CO2 Toward Green Engineering

Mechanical, Crystallization, Rheological, and Supercritical CO2 Foaming Properties of Polybutylene Succinate Nanocomposites: Impact of Carbon Nanofiber Content

Rheological Properties and Foam Preparation of Biodegradable Poly(butylene Succinate)

Low-shrinkage Biodegradable PBST/PBS Foams Fabricated by Microcellular Foaming Using CO2 & N2 As Co-Blowing Agents

An Ultra-High Volume Expansion Ratio and No-Shrinkage Poly(Butylene Adipate-co-Terephthalate) Foam: Compression and Resilience Properties

Review on poly (butylene succinate) foams: Modifications, foaming behaviors and applications

Effect of Poly(butylenes Succinate) on Poly(lactic Acid) Foaming Behavior: Formation of Open Cell Structure

Biodegradable PLA/PBS open-cell foam fabricated by supercritical CO2 foaming for selective oil-adsorption

High-Strength Bio-Degradable Polymer Foams with Stable High Volume-Expansion Ratio Using Chain Extension and Green Supercritical Mixed-Gas Foaming

Study on the Foaming Behaviors of PBS and Its Modification with PA6IcoT Assisted by scCO 2

Effect of Processing Conditions on Poly(butylene Succinate) Foam Materials

Biodegradable Ultra-Large Expansion and High Open-Cell PLA/PBAT Foams Fabricated by Supercritical CO2 Foaming for Selective Oil/Water Absorption

Biodegradable and Ultra-High Expansion Ratio PPC-P Foams Achieved by Microcellular Foaming Using CO2 as Blowing Agent

Foaming Behaviors of Poly (butylene Adipate-Co-terephthalate) with Methyl Methacrylate-Co-glycidyl Methacrylate As Chain Extender

Supercritical CO2 extrusion foaming of highly open-cell poly(lactic acid) foam with superior oil adsorption performance