Effect of Grinding Liberation on Recovery of Silicon from MG-Si Waste Slag by Flotation

Wei, Kuixian

DOI: https://doi.org/10.1007/s12633-024-02960-7

IF: 3.4

2024-03-27

Silicon

Abstract:Metallurgical-grade silicon-refined waste slag (MGSRS) was produced during the MG-Si refining production process, which occupies huge amounts of land resources, caused the loss of nearly 110,000 tons of MG-Si every year. Therefore, it is of great significance to recover the elemental silicon from MGSRS. However, because silicon is tightly wrapped by slag and difficult to separate, this resulting in the difficulty of silicon recovery. In this study, silicon recovery powders were obtained through the process of grinding liberation and flotation separation. The effect of grinding time on the liberation of MGSRS and the flotation recovery of silicon was studied. The liberation mechanism of MGSRS was further discussed. The results showed that the liberation degree of silicon particles was 79.45% (grinding for 15 min), which was 7.94% higher than that of silicon particles after 5 min grinding time, and 77.15% of the silicon particles were fully liberated. The flotation recovery of silicon can increase from 10.5 to 78.7% with the appropriate collector. Mechanism study showed that during the grinding process, silicon was separated along the (111) surface, and Ca 2 Al 2 SiO 7 had the largest amount of liberation along the (211) plane. More unsaturated sites of aluminum and calcium ions were observed on the silicate surface, which were favorable for adsorption with the reagent and beneficial to the silicon recovery. These results indicated that the silicon and slag of MGSRS can be sufficiently separated through grinding and flotation, and the purity of recovered silicon was about 70%. The silicon resources in MGSRS were recovered economically and could be used as the raw materials for the preparation of silicon alloy and high purity silicon.

materials science, multidisciplinary,chemistry, physical