Abstract:Solar grade silicon (SoG-Si) is the core material of solar cells. The removal of boron (B) has always been a challenge in the preparation of high purity Si. Slag refining has always been considered as one of the effective methods to remove B, but the design of refined slag has been limited by the cognition of the relationship between slag structure and impurity removal, and can only rely on the apparent basicity and oxygen potential adjustment of slag based on a large number of conditional experiments. In order to clarify the B removal mechanism of slag refining from Si, nuclear magnetic resonance (NMR) and Raman vibrational spectroscopy were used to investigate in detail the behavior and state of B and aluminum (Al) in the SiO2–CaO–Al2O3–B2O3 slag. The role of the degree of B–Si cross linking on the B activity in slag was highlighted by comparing the partition ratio (LB) between slag and Si. Q2 structural unit of slag is an important site for capturing B. BO4 (1B, 3Si) species is the main form of connection between B and silicate networks, which determines the activity of B in the slag. The addition of Al2O3 into SiO2–CaO slag can change the relative fraction of Q2 and BO4 (1B, 3Si). Increasing Al2O3 content from 0 to about 20 wt% can lead to the overall increase of Q2 population, and a tendency to decrease first and then increase of BO4 (1B, 3Si) fraction under both basicity conditions (0.6 and 1.1). When Al2O3 content is less than 10 ± 1 wt%, the decrease of BO4 (1B, 3Si) population plays a major role in deteriorating the connectivity between B and aluminosilicate network, which leads to a higher activity of B. When the Al2O3 content is greater than 10 ± 1 wt%, B is incorporated into the silicate network more easily due to the formation of more Q2 and BO4 (1B, 3Si), which contributes to a rapid decline in activity of B in slag.

Effects of Slag Treatment Conditions on Boron Removal from Metallurgical Silicon by United Gas-Slag Refining Technology

Boron Removal from Industrial Silicon by Combined Slagging and Acid Leaching Treatment Technology

Removal of impurities from metallurgical grade silicon by addition of ZnO to calcium silicate slag

Mechanism of Boron Removal Using Calcium Silicate Slag Containing CaCl2 under O2 Atmosphere

Reaction Mechanism and Kinetics of Boron Removal from Molten Silicon via CaO-SiO2-CaCl2 Slag Treatment and Ammonia Injection

Boron Removal from Silicon Using Secondary Refining Techniques by Metallurgical Method

Preparation of Low-Boron Silicon from Diamond Wire Sawing Waste by Pressure-Less Sintering and CaO–SiO2 Slag Treatment

Design of Refining Slag Based on Structural Modifications Associated with the Boron Removal for SoG-Si

Boron removal from silicon melt by gas blowing technique

Recovery and Purification of Metallic Silicon from Waste Silicon Slag in Electromagnetic Induction Furnace by Slag Refining Method

Separating and Recycling of Elemental Silicon from Wasted Industrial Silicon Slag

Effect of Refining Slag Composition on the Cleanliness of Oriented Silicon Steel

Enhancing the separation of Fe/Al/Ca impurities from metallurgical silicon to purify by slagging-directional solidification

Application of Pressure-less Sintering and Dynamic-Slag Treatment to Recover Diamond Wire Saw Silicon Powder

High-value Recycling of Photovoltaic Silicon Waste: Accelerated Removal of Impurity Boron Through Na3AlF6-enhanced Slag Refining

Study of the Preparation of High Purity Silicon by a New Electro-thermal Metallurgy Method

Recycling of carbonized rice husk for producing high purity silicon by the combination of electric arc smelting and slag refining

Effect of Grinding Liberation on Recovery of Silicon from MG-Si Waste Slag by Flotation

Oxide unlocking electron beam melting to separate boron for impurities co-removal of metallurgical grade silicon

Separation and purification of silicon from cutting kerf-loss slurry waste by electromagnetic and slag treatment technology

Recovery of titanium, aluminum, magnesium and separating silicon from titanium-bearing blast furnace slag by sulfuric acid curing—leaching