Abstract:Solar grade silicon (SoG-Si) is the core material of solar cells. The removal of boron (B) has always been a challenge in the preparation of high purity Si. Slag refining has always been considered as one of the effective methods to remove B, but the design of refined slag has been limited by the cognition of the relationship between slag structure and impurity removal, and can only rely on the apparent basicity and oxygen potential adjustment of slag based on a large number of conditional experiments. In order to clarify the B removal mechanism of slag refining from Si, nuclear magnetic resonance (NMR) and Raman vibrational spectroscopy were used to investigate in detail the behavior and state of B and aluminum (Al) in the SiO2–CaO–Al2O3–B2O3 slag. The role of the degree of B–Si cross linking on the B activity in slag was highlighted by comparing the partition ratio (LB) between slag and Si. Q2 structural unit of slag is an important site for capturing B. BO4 (1B, 3Si) species is the main form of connection between B and silicate networks, which determines the activity of B in the slag. The addition of Al2O3 into SiO2–CaO slag can change the relative fraction of Q2 and BO4 (1B, 3Si). Increasing Al2O3 content from 0 to about 20 wt% can lead to the overall increase of Q2 population, and a tendency to decrease first and then increase of BO4 (1B, 3Si) fraction under both basicity conditions (0.6 and 1.1). When Al2O3 content is less than 10 ± 1 wt%, the decrease of BO4 (1B, 3Si) population plays a major role in deteriorating the connectivity between B and aluminosilicate network, which leads to a higher activity of B. When the Al2O3 content is greater than 10 ± 1 wt%, B is incorporated into the silicate network more easily due to the formation of more Q2 and BO4 (1B, 3Si), which contributes to a rapid decline in activity of B in slag.

Mechanism of Boron Removal Using Calcium Silicate Slag Containing CaCl2 under O2 Atmosphere

Reaction Mechanism and Kinetics of Boron Removal from Molten Silicon via CaO-SiO2-CaCl2 Slag Treatment and Ammonia Injection

Boron Removal from Industrial Silicon by Combined Slagging and Acid Leaching Treatment Technology

Effects of Slag Treatment Conditions on Boron Removal from Metallurgical Silicon by United Gas-Slag Refining Technology

Boron Removal from Silicon Using Secondary Refining Techniques by Metallurgical Method

Removal of impurities from metallurgical grade silicon by addition of ZnO to calcium silicate slag

A First-Principles Investigation into the Adsorption Behavior and Deposition Mechanism of Boron-Containing Gases on Si(100) Surfaces During Chemical Vapor Deposition

Design of Refining Slag Based on Structural Modifications Associated with the Boron Removal for SoG-Si

Oxide unlocking electron beam melting to separate boron for impurities co-removal of metallurgical grade silicon

Physicochemical Conditions of Boron–Siliconizing of Molybdenum-Based Alloys in Chlorine and Fluorine Medium

Mechanism of boron removal of primary Si phases and morphology evolution of impurity phases during slow cooling solidification refining of Al-30wt.%Si alloy with Zr additions

Recycling silicon kerf waste: Use cryolite to digest the surface oxide layer and intensify the removal of impurity boron

Enhanced boron removal by CrMnFeNi-based high-entropy alloys during purification of silicon

Kinetics study on the low-temperature soda roasting of boron-rich blast furnace slag

Combining experimental analyses and molecular dynamics simulations in impurity removal at the Si/slag interface

Effects of boron addition on the high temperature oxidation of MoSi2 alloys

Competitive crystallization of B, Si, and Mg and two-stage separation of olivine and suanite from boron-bearing slag in supergravity field

A novel method for efficient recovery of boron from boron-bearing iron concentrate: Mineral phase transformation and low-temperature separation via super-gravity

Distribution of Iron and Boron Between Silicon Metal Smelting Products in Industrial Saf using Borate Fluxes

Preparation of boric acid and magnesium hydroxide from boron-rich slag by hydrochloric acid leaching method

Reduction of oxygen during the crystal growth in heavily antimony-doped Czochralski silicon