Abstract:316 stainless steel (SS) was coated with CoCrFeNiNbx (x: atomic ratio, x = 0, 0.1, 0.2, and 0.3) high entropy alloy coatings (HEACs) by laser cladding (LC). The impacts of Nb content on the phase composition, microstructure, microhardness, wear resistance and corrosion properties of CoCrFeNi based HEACs were examined. Different from the canonical dendritic (DR) - interdendritic (ID) microstructure presented by the other three HEACs, the ID of Nb0.3 HEACs also existed nanoscale Nb-rich Laves phase composed of Nb-Ni and Nb-Co. The inclusion of Nb significantly reduced the average grain size of CoCrFeNi based HEACs from 59.43 mu m to 11.38 mu m. It also greatly diminished the formation of high angle grain boundaries (HAGBs), increasing the percentage of low angle grain boundaries (LAGBs) from 31 % to 61 %. The microhardness of Nb-containing HEACs was significantly promoted due to the solid solution strengthening and fine grain strengthening caused by large size Nb atoms. Affected by Laves phase with high coordination number and space filling ratio and higher proportion of LAGBs, the microhardness of Nb0.3 HEAC was even as high as 530 HV. The increase in Nb concentration also strengthened the HEACs' resistance to wear. Nb0, Nb0.1, Nb0.2, and Nb0.3 HEACs had corresponding specific wear rates of 0.36, 0.32, 0.23, and 0.20 mm3/Nm. Unlike 316 SS, Nb0 and Nb0.1 HEACs, which had both adhesive wear and abrasive wear, Nb0.2 and Nb0.3 HEACs were mainly wear by abrasive wear. The corrosion behavior of CoCrFeNiNbx HEACs in 0.5 M H2SO4 solution was similar to 316 SS, but the corrosion resistance was stronger than 316 SS. Nb0.3 HEAC with the Ecorr of -164 mV and Icorr of 6.40 x 10-7 A/cm2 showed the best acid corrosion resistance, which could be attributed to the stable and dense passivation film on its surface. Distinct from the intergranular corrosion of other coatings, the corrosion of Nb0.3 HEAC mainly occurred in DR, because the FCC phase acted as the anode site in it when FCC and Laves phase co-existed.

The influence of sulphide on the ultrasonic cavitation erosion-corrosion behaviors of HVOF-sprayed WC-Cr 3 C 2 -Ni coating

Effect of 3.5 % NaCl solution with different Na 2 S concentrations on ultrasonic cavitation erosion behaviors of HVOF sprayed WC-Ni coatings

Electrochemical Corrosion Behavior in Sulfuric Acid Solution and Dry Sliding Friction and Wear Properties of Laser-Cladded CoCrFeNiNb High Entropy Alloy Coatings

Hydro-abrasive Erosion and Cavitation-Silt Erosion Characteristics of HVOF Sprayed WC-Ni Cermet Coatings under Different Flow Velocities and Sand Concentrations

Influences of Sand Concentration and Flow Velocity on Hydro-Abrasive Erosion Behaviors of HVOF Sprayed Cr3C2–NiCr and WC–Cr3C2–Ni Coatings

Comparison on Long-Term Corrosion Performance of WC-CoCr and Al2O3-TiO2 Ceramic Coatings in Sulphide-Containing 3.5 Wt% NaCl Solution

Cavitation-silt erosion behavior and mechanism in simulated sea water slurries of cermet coatings manufactured by HVOF spraying

Effects Of Wc Crystal Characteristics On Microstructure And Mechanical Property Of Hvof-Sprayed Wc-Cocr Coatings

Resistance of HVOF-Sprayed Cr3C2-25NiCr and WC-10CO-4Cr coatings to cavitation and erosion by mud jetting

Effects of microstructure and mechanical properties on cavitation erosion resistance of NiCrWMoCuCBFe coatings

Cold-sprayed Cu Matrix Composite Coatings with Core-Shell Structured Co@WC Reinforcements on Q235 Steel

Tribocorrosion behavior of HVOF sprayed WC-based cermet coatings in sodium chloride solution environment in relation to binder phases

Corrosive wear behavior of HVOF-sprayed micro-nano-structured Cr3C2–NiCr cermet coatings under aqueous media

Influence of ultrasonic assistance on the microstructure and friction properties of laser cladded Ni60/WC composite coatings

Cavitation erosion resistance in NaCl medium of HVOF sprayed WC-based cermet coatings at various flow velocities: A comparative study on the effect of Ni and CoCr binder phases

Effect of prolonged immersion on corrosion and cavitation resistance of HVOF-sprayed WC-NiCr and WC-Hastelloy cermet coatings

Slurry erosion behaviour and mechanism of HVOF sprayed micro-nano structured WC-CoCr coatings in NaCl medium

Evaluation of cavitation/corrosion synergy of the Cr3C2-25NiCr coating deposited by HVOF process

Cavitation erosion characteristics at various flow velocities in NaCl medium of carbide-based cermet coatings prepared by HVOF spraying

Effect of the microstructure of corrosion products on tribo-corrosion performance of HVOF-sprayed NiCrWMoCuCBFe coating

Cavitation Erosion Behavior of Co-28Mo-8Cr-2Si Coating in Deionized Water and Artificial Seawater