Abstract:Wear and slurry erosion are common problems in the operation of underwater components. Preventive maintenance can extend the service life of underwater components and increase the working efficiency. CoCrFeNi + x (NbC) (x = 5 wt%, 10 wt% and 15 wt%) high entropy alloys (HEAs) composite coatings were prepared on the surface of 316 stainless steel (SS) commonly acted as underwater components combined with laser cladding (LC). The microstructure, wear and slurry erosion behaviors of the coatings were investigated. During the solidification, NbC could serve as the nucleation site for non-uniform nucleation and play a pinning role, promoting the formation of fine equiaxed grains and refining the grains of the composite coatings greatly. The average grain size decreased from 52.19 μm of Nb-free coating to 12.85 μm of CoCrFeNi + 15 wt% NbC composite coating. NbC also promoted the formation of low angle grain boundaries (LAGBs) and geometrically necessary dislocations (GND), the LAGBs of CoCrFeNi + 15 wt% NbC composite cladding layer reached 63.4% with ρ GND up to 1.51 × 10 15 m −2 . CoCrFeNi + 10w.% NbC coating achieved higher microhardness (450.8 ± 5 HV 0.2 ) thanks to the combined action of various strengthening mechanisms. Simultaneously, it obtained stronger wear resistance, with a specific wear rate of 0.17 × 10 −4 mm 3 /Nm. In addition to oxidative wear, abrasive wear and adhesive wear coexisted on its worn surface. In slurry erosion test, the cumulative mass loss of CoCrFeNi + 10 wt% NbC HEAs composite coating was the lowest in each cycle and grew more slowly due to its higher microhardness and uniform distribution of reinforcement phases. The erosion mode of 316 SS and CoCrFeNi coating was mainly ductile fracture, while NbC-containing composite coatings exhibited a failure mode combining brittleness and ductility.

Cavitation-silt erosion behavior and mechanism in simulated sea water slurries of cermet coatings manufactured by HVOF spraying

Hydro-abrasive Erosion and Cavitation-Silt Erosion Characteristics of HVOF Sprayed WC-Ni Cermet Coatings under Different Flow Velocities and Sand Concentrations

Influences of Sand Concentration and Flow Velocity on Hydro-Abrasive Erosion Behaviors of HVOF Sprayed Cr3C2–NiCr and WC–Cr3C2–Ni Coatings

Cavitation erosion resistance in NaCl medium of HVOF sprayed WC-based cermet coatings at various flow velocities: A comparative study on the effect of Ni and CoCr binder phases

Cavitation erosion characteristics at various flow velocities in NaCl medium of carbide-based cermet coatings prepared by HVOF spraying

Performance evaluation of HVOF sprayed WC-10Co4Cr coatings under slurry erosion

Effect of 3.5 % NaCl solution with different Na 2 S concentrations on ultrasonic cavitation erosion behaviors of HVOF sprayed WC-Ni coatings

Cavitation Erosion Behavior of Co-28Mo-8Cr-2Si Coating in Deionized Water and Artificial Seawater

Slurry erosion behaviour and mechanism of HVOF sprayed micro-nano structured WC-CoCr coatings in NaCl medium

Resistance of HVOF-Sprayed Cr3C2-25NiCr and WC-10CO-4Cr coatings to cavitation and erosion by mud jetting

The influence of sulphide on the ultrasonic cavitation erosion-corrosion behaviors of HVOF-sprayed WC-Cr 3 C 2 -Ni coating

Cavitation erosion behavior of HVAF-sprayed Cu-based glassy composite coatings in NaCl solution

Effect of prolonged immersion on corrosion and cavitation resistance of HVOF-sprayed WC-NiCr and WC-Hastelloy cermet coatings

Cavitation Erosion Investigations of Hard Carbide and Nitride Based Novel Coatings Manufactured by Plasma Spraying

Investigations of cavitation erosion and wear resistance of cermet coatings manufactured by HVOF spraying

Tribological and electrochemical properties of Cr–Si–C–N coatings in artificial seawater

Comparison of the Resistance to Cavitation Erosion and Slurry Erosion of Four Kinds of Surface Modification on 13-4 Ca6NM Hydro-Machinery Steel

Effect of Initial Surface Roughness on Cavitation Erosion Resistance of Arc-Sprayed Fe-Based Amorphous/Nanocrystalline Coatings

CAVITATION EROSION BEHAVIOR OF WC–Co COATINGS ON TURBINE STEEL DEPOSITED BY COLD SPRAY

Comparison on multi-angle erosion behavior and mechanism of Cr3C2-NiCr coatings sprayed by SPS and HVOF

Exploration of wear and slurry erosion mechanisms of laser clad CoCrFeNi + x (NbC) high entropy alloys composite coatings