Synthesis and thermophysical performances of (Nd1-xYbx)2AlTaO7 oxides for heat-insulation coating applications

Zhang Qian,Lu Kui,Wang Shi-Huai,Zhang Hongsong,Yan Xianfeng,Sang Weiwei,Zhao Yongtao,Tang An

DOI: https://doi.org/10.1016/j.ceramint.2020.07.149

IF: 5.532

2020-12-01

Ceramics International

Abstract:A series of novel (Nd1-xYbx)2AlTaO7 oxides for thermal barrier coating application were synthesized exploring multi-step solid state clotting technology, the phase composition and thermophysical performances were analyzed. Results show that with increasing Yb2O3 content, the obvious phase transformation from weberite lattice to pyrochlore structure can be found. Owning to influence of oxygen vacancy, thermal conductivity of obtained products is less than that of 8YSZ. The thermal conductivity for (Nd1-xYbx)2AlTaO7 oxides decreases gradually with increasing Yb2O3 content, and (Nd0.3Yb0.7)2AlTaO7 has the lowest value. For (Nd1-xYbx)2AlTaO7 (x = 0, 0.1, 0.3) oxides, the lattice-energy has primary influence on thermal expansion coefficient, and electro-negativity governs the thermal expansion coefficient of (Nd1-xYbx)2AlTaO7 (x = 0.5, 0.7, 0.9 and 1) oxides. Thermal expansion coefficient of obtained oxides is close to that of 8YSZ.

materials science, ceramics

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is to develop new thermal barrier coating materials to improve the effective protection of turbine blades and other high - temperature components. Specifically, the research focuses on synthesizing and evaluating a series of new (Nd\(_{1 - x}\)Yb\(_x\))\(_2\)AlTaO\(_7\) oxides for thermal barrier coating applications. These problems can be summarized as follows:

1. **Reducing Thermal Conductivity**: The currently commonly used yttria - stabilized zirconia (YSZ) ceramics will undergo a phase change at high temperatures, causing the coating to peel off prematurely. Therefore, a material with lower thermal conductivity needs to be found to improve thermal insulation performance and durability.

2. **Matching the Coefficient of Thermal Expansion**: The newly developed material should have a coefficient of thermal expansion similar to that of the metal substrate to reduce the stress and crack propagation caused by thermal expansion mismatch.

3. **High - Temperature Stability**: The new material should maintain a stable crystal structure within the working temperature range and avoid phase changes and volume changes.

### Research Methods

To achieve the above - mentioned goals, the researchers synthesized (Nd\(_{1 - x}\)Yb\(_x\))\(_2\)AlTaO\(_7\) oxides by using a multi - step solid - state sintering technique and carried out a detailed analysis of their phase composition and thermophysical properties. The research contents include:

- **Phase Structure Transformation**: As the content of Yb\(_2\)O\(_3\) increases, the material gradually transforms from the weberite structure to the pyrochlore structure.

- **Thermal Conductivity**: By introducing oxygen vacancies and mass fluctuations, the thermal conductivity is reduced. The experimental results show that (Nd\(_{0.3}\)Yb\(_{0.7}\))\(_2\)AlTaO\(_7\) has the lowest thermal conductivity.

- **Coefficient of Thermal Expansion**: For (Nd\(_{1 - x}\)Yb\(_x\))\(_2\)AlTaO\(_7\) oxides with different compositions, the coefficient of thermal expansion is affected by lattice energy and electronegativity. It is found that the coefficient of thermal expansion of these oxides is close to that of YSZ.

### Conclusions

Through this research, the authors successfully prepared (Nd\(_{1 - x}\)Yb\(_x\))\(_2\)AlTaO\(_7\) oxides and confirmed that they have lower thermal conductivity and a coefficient of thermal expansion similar to that of YSZ, showing the potential as new thermal barrier coating materials. In particular, (Nd\(_{0.3}\)Yb\(_{0.7}\))\(_2\)AlTaO\(_7\) performs excellently in terms of thermal conductivity and is expected to be further applied to thermal barrier coatings in high - temperature environments.

### Key Formulas

1. **Thermal Conductivity Calculation Formula**:
\[
\kappa=\alpha\cdot C_p\cdot\rho
\]
where \(\alpha\) is the thermal diffusivity, \(C_p\) is the specific heat capacity, and \(\rho\) is the density.

2. **Effect of Ionic Radius Ratio on Crystal Structure**:
\[
R_{RE / B}=\frac{(R_{Nd}^{1 - x}+R_{Yb}^x)}{R_{Ta}}
\]
where \(R_{Nd}\) and \(R_{Yb}\) are the effective ionic radii of Nd\(^{3+}\) and Yb\(^{3+}\) respectively, and \(R_{Ta}\) is the ionic radius of Ta\(^{5+}\).

3. **Relationship between Coefficient of Thermal Expansion and Lattice Energy**:
\[
U = \frac{N e^2 Z^2}{4\pi\epsilon_0 R}
\]
where \(N\) is Avogadro's constant, \(e\) is the electron charge, \(Z\) is the ionic charge, and \(R\) is the average distance between particles.

Through these studies, the paper provides important theoretical and experimental bases for the development of high - performance thermal barrier coating materials.