Abstract:LaMgAl11O19 (LMA) with magnetoplumbite structure has been identified as a potential candidate for the next generation of thermal barrier coatings (TBCs). However, the as-sprayed LMA coating presents a large amount of amorphous phase originating from the rapid quenching from the molten droplets, which may compromise the reliability of coating during high-temperature service. A logical approach to improve LMA TBC life, therefore, is to enhance its crystallinity. In the present study, three LMA powders with different particle size distributions (fine, medium and coarse feedstocks) were utilized to deposit TBCs to investigate whether the thermal durability of LMA can be improved by increasing particle size. It was based on a hypothesis that large particle size can decrease the melting degree of in-flight particles and thus result in high crystallinity of as-sprayed LMA coating, making less recrystallization stress to enhance the thermal shock resistance of LMA coating. Results show that prolonged thermal cycling durability can indeed be achieved by increasing particle size. However, excessive particle size could lead to higher porosity derived from unmelted particles, which function as the weak regions for the coating system, thereby damaging the structural integrity and adhesive strength between the topcoat and bond coat. This could cause microcrack linking when the accumulated thermal stress exceeds its fracture toughness under consecutive heating-cooling cycles despite its higher crystallinity. Concerning the coating fabricated by medium powder, it achieves the optimal balance of crystallinity and structure integrity, resulting in the longest thermal cycling lifetime. The results provide guidance for the development and design of high thermal durability LMA TBCs. When optimizing the recrystallization stress within the coating, attention should be paid to improving its bonding strength simultaneously.

Influence of Ln3+ and B3+ Ions Co‐Substitution on Thermophysical Properties of LnMB11O19‐type Magnetoplumbite LaMgAl11O19 for Advanced Thermal Barrier Coatings

Thermo-physical Properties of Rare-Earth Hexaaluminates LnMgAl11O19 (ln: La, Pr, Nd, Sm, Eu and Gd) Magnetoplumbite for Advanced Thermal Barrier Coatings

Low Thermal Conductivity Sr 2+ , Zn 2+ and Ti 4+ Ions Co-Doped LaMgAl 11 O 19 for Potential Thermal Barrier Coating Applications

Improvement on thermophysical and mechanincal properties of LaMgAl11O19 magnetoplumbite by Nd2O3 and Sc2O3 co-doping

Influence of Divalent Me2+ on Phase Structures and Thermophysical Properties of Magnetoplumbite Type LaMgAl11O19

Enhanced anti‐deliquescent property and ultralow thermal conductivity of magnetoplumbite‐type LnMeAl11O19 materials for thermal barrier coating

Multi-Enhanced-Phonon Scattering Modes in Ln-Me-A Sites Co-Substituted LnMeA11O19 Ceramics

Microstructures, thermophysical properties and thermal cyclic behaviors of Nd2O3 and Sc2O3 co-doped LaMgAl11O19 thermal barrier coating deposited by plasma spraying

Synthesis and Characterization of LaMgAl11O19 As Thermal Barrier Coatings Material

Synthesis and Thermo-physical Properties of Novel La2-xGdxWMoO9 Ceramics for Thermal Barrier Coatings

Phase Transformation Inhibition and Improved Thermo-Mechanical Properties of Rare Earth Niobates for Thermal Barrier Coatings

Prolonged thermal durability of plasma-sprayed lanthanum hexaluminate thermal barrier coating by optimizing crystallinity

Synthesis and thermophysical performances of (Nd1-xYbx)2AlTaO7 oxides for heat-insulation coating applications

Lanthanum–titanium–aluminum oxide: A novel thermal barrier coating material for applications at 1300°C

High Pr-content (Tb0.2Pr0.8)(Fe0.4Co0.6)1.93−xBx magnetostrictive alloys

A Promising Lasmzr2o7 Ceramic with Pyrochlore Structure for Thermal Barrier Coatings

The effect of co-substitution on the microwave dielectric properties of Ba6-3Nd8+2Ti18O54(x=2/3) ceramics

Bivalent Sr2+ doping to improve room-temperature TCR of La0.8-Sr Ag0.2MnO3 polycrystalline ceramics

Structure and Properties of Nonstoichiometric Y1-xNbxO1.5+x for Thermal Barrier Coatings

Preparation and Thermophysical Properties of New Multi-Component Entropy-Stabilized Oxide Ceramics for Thermal Barrier Coatings

Effect of Bi doping on the crystal structure, magnetic and magnetocaloric properties of La0.7-Bi Sr0.15Ca0.15MnO3 (x = 0, 0.05, 0.10, 0.15) manganites