Influence of Divalent Me2+ on Phase Structures and Thermophysical Properties of Magnetoplumbite Type LaMgAl11O19

HR Lu,XJ Guo,CG Zhang,CA Wang
2015-01-01
Rare Metal Materials and Engineering
Abstract:Magnetoplumbite-type LaMeAl11O19 (Me=Mg; Mn; Ni; Cu; Zn) materials are promising candidates to replace yttria partially stabilized zirconia as a thermal barrier coating material for Ni-based superalloy due to their complex crystal structure, high melting point, low sintexability and relative low intrinsic thermal conductivity. The series of samples were synthesized through citric acid sol-gel route according to the formula LaMeAl11O19(Me=Mg; Mn; Ni; Cu; Zn) using La(NO3)(3)center dot 6H(2)O, Me(NO3)(2)center dot 6H(2)O and Al(NO3)(3)center dot 9H(2)O as starting materials. The thermal behavior, phase compositions, Raman spectra and microstructure/electron diffraction patterns were characterized by DSC-TG, X-ray diffraction, Raman spectrometer, scanning electron microscopy (SEM), and transmission electron microscope (TEM) with selected area electron diffraction (SAED), respectively. The effect of divalent Me2+ on the phase composition of LaMeAl11O19 was studied. The influence of enhanced phonon scattering contributed by the changed Me2+ coordination environment on the thermal conductivities of LaMeAl11O19 ceramic materials was analyzed. The results indicate that all the LaMeAl11O19 compositions are composed of pure magnetoplumbite LaMeAl11O19 phase. The thickness along c-axis direction of platelet-like crystal varies with the type of divalent Me2+. The thermal conductivities of LaMeAl11O19 ceramics decrease with increasing Me2+ atomic number and the average molar mass.
What problem does this paper attempt to address?