Tailoring the thermal conductivity of Sc2O3–Yb2O3 Co-stabilized ZrO2 thermal barrier materials and mechanism insight

Jing Zhang,Zhi-Gang Wang,Xiwen Song,Min Xie,Yonghe Zhang,Rende Mu,Shengli An

DOI: https://doi.org/10.1016/j.ceramint.2022.12.236

IF: 5.532

2023-05-01

Ceramics International

Abstract:The present work aims to develop a novel thermal barrier coating (TBC) material for potential applications above 1400 °C. Specifically, novel Yb x Sc y Zr1-x-y O2 (y = 0.02, 0.04, 0.06; x + y = 0.05, 0.06, 0.07) ceramics with tailored thermal conductivity consist of mixtures of tetragonal and cubic phases. The cubic phase ratio of Yb x Sc y Zr1-x-y O2 ceramics gradually increase with an increase of Yb2O3 content. The thermal conductivity of Yb x Sc y Zr1-x-y O2 ceramics decreases with the increase of Yb2O3 and Sc2O3 doping. When the total dopant content is kept constant, the thermal conductivity of the specimens with higher Yb2O3 content is lower than those of the specimens with low Yb2O3 content. Quantitative results indicate that the phonon scattering associated with the elastic field around a point imperfection plays a dominant role in the reduction of thermal conductivity. These results suggest that the co-doing of Sc2O3 and Yb2O3 provides a feasible path to achieve low thermal conductivity.

materials science, ceramics