Phase evolution and thermophysical properties of high‐entropy RE 2 (Y 0.2 Yb 0.2 Nb 0.2 Ta 0.2 Ce 0.2 ) 2 O 7 oxides

Liang Xu,Lei Su,Hongjie Wang,Min Niu,Lei Zhuang,Kang Peng,Xingyu Fan,Hongfei Gao,De Lu
DOI: https://doi.org/10.1111/jace.18509
IF: 4.186
2022-04-26
Journal of the American Ceramic Society
Abstract:Pursuing novel thermal barrier coating materials with lower thermal conductivity and high‐temperature stability can simultaneously improve the working efficiency and service temperature of gas turbine. In this study, a series of high‐entropy RE2(Y0.2Yb0.2Nb0.2Ta0.2Ce0.2)2O7 (RE = La, Nd, Sm, Gd, Dy, and Er) oxides were prepared though solid‐state reaction. Through tuning the rare‐earth cations, an order‐disorder transition occurs from certain partially ordered weberite structure (C2221) to disordered defective fluorite structure (Fmࣥ3m). All the high‐entropy RE2(Y0.2Yb0.2Nb0.2Ta0.2Ce0.2)2O7 oxides possess low thermal conductivity at the range of 0.91–1.34 W·m−1·K−1 at room temperature, which can be attributed to increased lattice anharmonicity and disorder, resulting in additional phonon scattering. Herein, we proved that the incorporation of heterovalent cations at B‐sites in high‐entropy A2B2O7 crystals is an effective strategy to reduce the thermal conductivity without compromising decrease of oxygen vacancy. Moreover, the high‐entropy RE2(Y0.2Yb0.2Nb0.2Ta0.2Ce0.2)2O7 oxides show the relatively higher thermal expansion coefficients of 10.3‐10.7 × 10−6°C−1 and excellent phase stability at elevated temperature.This article is protected by copyright. All rights reserved
materials science, ceramics
What problem does this paper attempt to address?