Toward Novel Biocomposites from Unavoidable Food Supply Chain Wastes and Zirconia

Yang Gao,Fangru Xing,Menaka Jha,Krishna K. Yadav,Ranjana Yadav,Avtar S. Matharu

DOI: https://doi.org/10.1021/acssuschemeng.0c04211

2020-08-24

Abstract:The synthesis and characterization of novel biocomposites, herein termed bioboards, derived from agricultural residues (wheat straw and barley straw) and aqueous biosilicate solutions, as binder, are reported. The addition of a small amount of protein significantly enhances board strength. The internal bond strength (IBS) increases from 0.0498 to 0.0688 N mm^–2. Prior to adhesion, the agricultural residues were dewaxed (ethanol), making them more amenable to aqueous wetting. The aqueous biosilicate binder was obtained via KOH-assisted hydrothermal leaching of spent ashes derived from the combustion of wheat straw. The concentration of biosilicate was determined by ATR-IR spectroscopy and compared with commercial silicate solution (K120). Zirconia powders were introduced to increase the fireproof ability of bioboards. The presence of zirconia was evidenced by powder X-ray diffraction studies. Thus, the bioboards reported represent "greener" alternatives to conventional, commercial particle and medium density fiber boards because they are wood-free, use waste as a renewable resource (agricultural straws), and, importantly do not use any harmful phenol-formaldehyde and isocyanate binders.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c04211?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c04211</a>.Figure S1 for DSC traces, Figure S2 for IR bands, Figure S3 for TEM of zirconia powder, Figure S4 for fire retardant test (a) without ZrO₂ and (b) with ZrO₂, and Table S1 for flame retardancy data for state-of-art materials (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c04211/suppl_file/sc0c04211_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology