Production of sustainable wood-plastic composites from the nonmetals in waste printed circuit boards: Excellent physical performance achieved by solid-state shear milling

Shuangqiao Yang,Jun Jiang,Wenfeng Duan,Shibing Bai,Qi Wang

DOI: https://doi.org/10.1016/j.compscitech.2020.108411

IF: 9.1

2020-11-01

Composites Science and Technology

Abstract:<p>As a byproduct of electronic waste, the accumulated millions of tons of nonmetals from waste printed circuit boards (referred to hereinafter as NPCB) have caused severe environmental issues. Here, we report a novel method for the production of wood composites reinforced by NPCB via a solid-state shear milling (S³M) process. The S³M pretreatment successfully exfoliated NPCB into single glass fibers with a high aspect ratio. Hemicellulose and lignin were liberated from the surface of the wood cellulose fibers, and the size was reduced to a submicron level. Both optical and electron microscopy revealed that the wood composites prepared by the S³M process exhibited excellent filler dispersion and excellent interfacial adhesion between the filler and the polymer. This NPCB-reinforced wood composite was thermally stable at temperatures below 200 °C. In addition, the exfoliated NPCB and wood flour provided a well-designed structure that improved the tensile strength of the composite to 32.4 MPa. This wood composite retained a high storage modulus of 616 MPa at 100 °C, expanding the upper service temperature limit for wood composites. The excellent interfacial adhesion and hydrophilic nature of NPCB led to water absorption as low as 0.21%, exceeding the values previously reported for NPCB-reinforced wood composites under the same conditions. Finally, this wood composite also contained negligible organic pollutants and low heavy-metal concentrations, which are far below the regulatory limits for hazardous waste. The above results show that the reuse of NPCB in high-strength wood composites is a promising choice for both resolving environmental pollution and reusing solid waste to create value-added products.</p>

materials science, composites