Abstract:The use of biodegradable polymers as matrices in composites gives a wide range of applications, especially in niche areas. The assessment of the effect of the filler content on the change of mechanical properties makes it possible to optimize the composition for specific needs. Biochar was used as a filler in the studied composites with two different biodegradable blends as a matrix. Poly(1,4-butylene adipate-co-1,4-butylene terephthalate)/polylactide/biochar (PBAT/PLA/BC) and polylactide/poly[(R)-3-hydroxybutyrate-co-4-hydroxybutyrate]/biochar (PLA/P(3HB-co-4HB)/BC) composites with 0, 10, 15, 20 and 30 wt% of biochar underwent mechanical tests. The test results revealed a change in the properties of the composites related to the filler content. The results of the tensile test showed that increasing the biochar content increased the tensile modulus values by up to 100% for composites with 30 wt% of biochar, compared to unfilled matrices, and decreased the elongation associated with the breaking of PBAT/PLA and PLA/P(3HB-co-4HB) matrix composites. The elongation values at break of PBAT/PLA and PLA/(3HB-co-4HB) composites with 30 wt% biochar were reduced by 50% and 65%, respectively, compared to the unfilled matrices. PLA/P(3HB-co-4HB) matrix composites, in contrast to PBAT/PLA/BC, showed a decrease in tensile strength with the increases in filler content from 35.6 MPa for unfilled matrix to 27.1 MPa for PLA/P(3HB-co-4HB)/BC30 composites. An increase in filler content increased the brittleness of the composites regardless of the matrix used, as determined under the Charpy impact-test. This phenomenon was observed for all tested PLA/P(3HB-co-4HB) composites, for which the impact strength decreased from 4.47 kJ/m2 for the matrix to 1.61 kJ/m2 for the composite containing 30 wt% biochar. PBAT/PLA-based composites with 10 wt% of biochar showed slightly lower impact strength compared to the unfilled matrix, but composites with 30 wt% biochar showed 30% lower impact strength than PBAT/PLA. The complex viscosity value increased with increased filler content. For all composites tested on both polyester matrices, the viscosity decreased with increasing angular frequency.

Conversion from Bamboo Waste Derived Biochar to Cleaner Composites: Synergistic Effects of Aramid Fiber and Silica

Poly(Lactic Acid) Biocomposites Reinforced With Ultrafine Bamboo-Char: Morphology, Mechanical, Thermal, And Water Absorption Properties

Improvements in Compatibility and Properties of Biocomposites Modified Through Nanosilica Attachment

High Toughness Composite Films Produced from Zein and Bamboo Fibers Based on Incorporating Biochar: Effects of Alkali Treatment

Versatile biochar for wood‐plastic composites: Improving mechanical properties, dimensional and thermal stability

Intumescent-Grafted Bamboo Charcoal: A Natural Nontoxic Fire-Retardant Filler for Polylactic Acid (PLA) Composites

Development of Biodegradable Flame-Retardant Bamboo Charcoal Composites, Part I: Thermal and Elemental Analyses.

Effect of different amounts of bamboo charcoal on properties of biodegradable bamboo charcoal/polylactic acid composites

Exploring synergistic solid lubrication for enhanced tribological performance in biochar-reinforced aluminum matrix composites fabricated by induction sintering

Influence of bio-coupling agent on interfacial interlocking compatibility and toughness of ultrafine bamboo charcoal/polylactic acid composite film

Development Of Biodegradable Flame-Retardant Bamboo Charcoal Composites, Part Ii: Thermal Degradation, Gas Phase, And Elemental Analyses

Strengthening and flame retarding effect of bamboo fiber modified by silica aerogel on polylactic acid composites

Mechanical and Rheological Evaluation of Polyester-Based Composites Containing Biochar

Enhancement of Flame Retardancy and Mechanical Properties of Polylactic Acid with a Biodegradable Fire-Retardant Filler System Based on Bamboo Charcoal

Preparation of Plastics- and Foaming Agent-Free and Porous Bamboo Charcoal based Composites Using Sodium Silicate as Adhesives

Emerging application of biochar as a renewable and superior filler in polymer composites

Fabrication of Phytic Acid/Urea Co-Modified Bamboo Biochar and Its Application as Green Flame Retardant for Polylactic Acid Resins

Properties evaluation of biochar/high-density polyethylene composites: Emphasizing the porous structure of biochar by activation

Effect of Biochar Addition on Mechanical Properties, Thermal Stability, and Water Resistance of Hemp-Polylactic Acid (PLA) Composites

(Bio)degradable Biochar Composites of PLA/P(3HB-co-4HB) Commercial Blend for Sustainable Future—Study on Degradation and Electrostatic Properties

Pinewood biochar antistatic polymer composites: an investigation of electrical, mechanical, rheological and thermal properties