Abstract:In this investigation, hybrid AA2024 – Si3N4 (0–6 wt.% @ 2%) – SiC (2 wt.%) – graphite (2 wt.%) alloy composites have been fabricated as per design using the stir casting method. This follows evaluation of physical, mechanical, thermal, thermo-mechanical, fracture toughness, and sliding wear performance as per standards. The density and material stability of the alloy composites improves with reinforcement content while porosity and thermal conductivity show a diminishing trend. The mechanical characteristics improve considerably with reinforcement. The alloy composite having 6 wt.% Si3N4 particulates show maximum mechanical characteristics like ultimate tensile strength (212 MPa), percent elongation (13%), flexural strength (645 MPa), micro-hardness (127 HV), and impact strength (85 J). Fracture toughness was found to improve with Si3N4 particulate content and with crack length. The storage modulus and damping capacity of the alloy composites have shown an increasing trend with reinforcement content while the loss modulus shows a reverse trend. The specific wear rate and friction coefficient tend to diminish with Si3N4 particulate content under steady state conditions. The normal load significantly influences the specific wear rate of the alloy composites under the Taguchi experimental design. Worn out surface morphology analysis shows wear mechanisms like surface fatigue, ploughing, micro-cutting, three-body abrasion, etc. responsible for surface damage. EDAX spectrum shows elemental presence and mapping and XRD analysis shows the presence and distribution of various phases of alloy composites and counter-surface disc. It could be the potential material for various components like gear, piston, cylinder liner, etc.

Synergistic Effect of Ex Situ and In Situ Reinforcements on the Dry Reciprocating Wear Behavior of AA6061-B4C Composite Fabricated Using Varying K2TiF6 Flux Content

Processing and Evaluation of Mechanical Properties and Dry Sliding Wear Behavior of AA6061-B4C Composites

Effect of B4C and SiC nanoparticle reinforcement on the wear behavior and surface structure of aluminum (Al6063-T6) matrix composite

Multi-response optimisation of wear parameters of B4C reinforced Al-Fe-Si composites: Using Taguchi-grey relational analysis

Preparation and Characterization of In Situ (TiC-TiB2)/Al-Cu-Mg-Si Composites with High Strength and Wear Resistance

Influence of particulate B4C with high weight fraction on microstructure and mechanical behavior of an Al-based metal matrix composite

Modeling of wear performance and surface roughness of AA6061-T6/B4C composite under dry sliding conditions by RSM

Influence of the Reinforcement Phase Composition on the Structure and Abrasive Wear Resistance of Aluminum Matrix Composites Reinforced with B4C and SiC

Investigation on Microstructures and Mechanical Behavior of In-Situ Synthesized TiC and TiB Reinforced Ti6Al4V Based Composite

Fabrication and Dry Sliding Wear Behavior of in Situ Al–K2ZrF6–KBF4 Composites Reinforced by Al3Zr and ZrB2 Particles

Importance of Al2TiO5 particle on the mechanical and wear performance of stir cast AA6061 composite using Central Composite Design

Effect of Si3N4 Ceramic Particulates on Mechanical, Thermal, Thermo-Mechanical and Sliding Wear Performance of AA2024 Alloy Composites

In-situ TiB2-TiC reinforced Fe-Al composite coating on 6061 aluminum alloy by laser surface modification

Wear Behavior of Ti6Al4V Based Hybrid Composites Reinforced with TiB2(7.5%) + TiC (7.5%)

Evaluation of Wear Properties of Stir Cast AA7050 -10% B4C Ex Situ Composite through Fuzzy-TOPSIS MCDM Method

Dry sliding friction and wear properties of B4C particulate-reinforced Al-5083 matrix composites

Tribological behavior of in-situ nanosized TiB2 particles reinforced AZ91 matrix composite

Frictional-Wear Properties of In-situ TiB2 Reinforced 2014Al Composites

Effect of in situ TiC reinforcement and applied load on the high-stress abrasive wear behaviour of zinc–aluminum alloy

Wear Performance of TiB2-Reinforced AZ91 Magnesium Metal Matrix Composite Fabricated by Ultrasonic Stir-Casting Process

Influence of In Situ Titanium Diboride Particulate Reinforcement on Mechanical Properties of Aluminum–Silicon Based Metal Matrix Composites