Abstract:This research investigates damage initiation in multipass hot rolling of steel. Hot tensile tests are conducted to generate experimental data for developing Johnson–Cook material models. The developed models are then used to predict damage initiation for square‐to‐round and round‐to‐round bar hot rolling. Studies on rolling temperature and initial bar geometries are performed. Hot rolling processes have been extensively used to produce round bars by reducing the cross‐sectional area of continuously cast steel. The current trend toward increasing productivity often requires a more aggressive reduction per pass. Establishing safe and optimized hot rolling parameters must be determined to avoid damage while deforming the specific steel composition. Understanding the damage mechanism during the metal forming process is vital for product quality. Herein, a combined experimental and simulation approach is developed to track the evolution potential damage during hot bar rolling. Hot tension tests are conducted on as‐cast vanadium microalloyed 15V38 steel at different hot rolling temperatures and strain rate conditions to develop Johnson–Cook‐type material model. A thermomechanical finite element model is developed to simulate potential damage trends in a 12‐pass square‐to‐round and 8‐pass round‐to‐round standard industrial hot rolling process, employing damage criteria. Results are illustrated by creating a damage map at each rolling pass to determine the critical hot rolling conditions for damage initiation. Several parametric studies are also performed to illustrate the application of the suggested methodology for hot rolling process optimization. Results show that the probability of the damage initiation is higher at higher pass reductions and lower temperatures.

Heat Straightening Rolled Shapes

Heat Straightening Damaged Steel Plate Elements

What You Should Know About Heat Straightening Repair of Damaged Steel

Systematization of heat straightening process of stiffened plate by surface flattening

The Study of Controlled Cooling Technology and Warping of X65 Heavy Pipeline Plate

Research on the Hot Straightening Process of Medium-Thick Plates Based on Elastic-Viscoplastic Material Modeling

Crack mechanism and experimental verification on straightening of AZ31B magnesium alloy plate

The Causes and Control of Longitudinal Edge Cracks of the Plate

Damage Initiation of 15V38 Steel Bar during Square‐to‐Round Hot Rolling Process

Modeling heat treatment of steel parts

Experimental Characterization and Strengthening Mechanism of Process-Structure-property of Selective Laser Melted 316 L

Research on key technologies for straightening pocketed aircraft frame parts

A Study on Remaining Efficiency of Thermal Straightening after Block Lifting

Impact of Hot Bending on the High-Temperature Performance and Hydrogen Damage of 2.25Cr-1Mo-0.25v Steel

Deformation Patterns in Hydroforming of Thin-Walled Y-Shaped Tube

Study on Cracks and Process Improvement for Case Hardened Gear Shaft Straightening

Calculation method and analysis of residual stress in the strip bending roller straightening process

Analysis of Reasons for Straightening Fracture of 65Mn Steel Sheet after Spheroidizing Annealing in Metallurgical Saw Blade

A Stroke Model for Straightening Partially Heat-Treated Ball Screws with Complex Mechanical Properties

Numerical Investigation of the Damage Effect on the Evolution of Adiabatic Shear Banding and Its Transition to Fracture during High-Speed Blanking of 304 Stainless Steel Sheets

Inverse Identification Method for Determining Stress–strain Curves of Sheet Metals at High Temperatures