High-Efficiency Electrolyte for Li-Rich Cathode Materials Achieving Enhanced Cycle Stability and Suppressed Voltage Fading Capable of Practical Applications on a Li-Ion Battery

Depeng Song,Xiaolin Sun,Quanhai Niu,Qing Zhao,Cheng Wang,Li Yang,Yue Wu,Minmin Li,Takeo Ohsaka,Futoshi Matsumotoc,Jianfei Wu

DOI: https://doi.org/10.1021/acsami.0c14995

2020-10-20

Abstract:Li-rich cathodes have been in considerable attention for their high reversible capacity. However, they have serious problems like poor cycling with intense capacity decay and voltage fading, which restrict their access to practical applications. In this work, a facile and efficient strategy is proposed to alleviate these intrinsic issues with a high-efficiency electrolyte system. This special electrolyte enables Li-rich cathodes to deliver superior integrated performance with a high initial discharge capacity of 301 mAh·g^–1, outstanding cycling stability with a capacity retention of 88% at 0.5 C over 500 cycles, and a remarkable rate capability of 136 mAh·g^–1 at 5 C, respectively. What is more, the voltage fading is largely suppressed. Physical and electrochemical characterizations demonstrate that the robust CEI film formed on the cathode surface contributes to the improved electrochemical performance. This work provides a new approach to surmount defects of Li-rich materials and will largely promote their practical applications on Li-ion batteries.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c14995?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c14995</a>.XRD pattern of Li_1.2Mn_0.54Ni_0.13Co_0.13O₂ (LMNCO) material; surface EDS mapping of Mn, Ni, and Co elements of the LMNCO material; comparisons of EIS profiles after 1st, 50th, 150th, 200th, 250th, and 300th cycles; SEM morphology of the Li-anode after 500 cycles in F-E-F and commercial electrolytes; and radar plot for the comparison of Li-rich (employing the F-E-F electrolyte), LiFePO₄ and NCM 811 by six critical criteria for practical applications (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c14995/suppl_file/am0c14995_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology

What problem does this paper attempt to address?

The problems that this paper attempts to solve are several key challenges faced by lithium - rich (Li - rich) cathode materials in the application of lithium - ion batteries. Specifically, these problems include:

1. **Poor cycle stability**: Lithium - rich cathode materials show significant capacity decay after multiple charge - discharge cycles, which limits their practical applications.
2. **Severe voltage decay**: As the number of cycles increases, the average working voltage of the battery gradually decreases, which is known as the voltage decay phenomenon.
3. **Electrolyte decomposition at high voltages**: Traditional carbonate - based electrolytes are prone to parasitic reactions and oxidative decomposition at high voltages, resulting in a decline in battery performance.
4. **Poor structural stability**: Lithium - rich cathode materials will undergo irreversible phase transitions during cycling, such as transition - metal migration and surface - structure degradation, all of which will affect the performance of the battery.

To overcome the above problems, the paper proposes an efficient electrolyte system to improve the comprehensive performance of lithium - rich cathode materials by using highly fluorinated electrolytes. This electrolyte can:

- Increase the initial discharge capacity (reaching 301 mAh·g\(^{-1}\))
- Significantly improve cycle stability (the capacity retention rate is 88% after 500 cycles at a 0.5 C rate)
- Enhance rate performance (the discharge capacity is 136 mAh·g\(^{-1}\) at a 5 C rate)
- Greatly suppress voltage decay

In addition, physical and electrochemical characterization results show that this efficient electrolyte can form a stable fluorine - rich cathode - electrolyte - interface (CEI) film on the cathode surface, thereby improving electrochemical performance. This method provides a new approach for the practical application of lithium - rich cathode materials.